Abstract:The synthesis, characterization, and dielectric properties of a new kind of low-temperature cofired ceramic (LTCC) composition based on Li 2O-Nb2O5-TiO2 system have been reported. The LNT ceramics were obtained by conventional mixed oxide route from the high-purity oxide powder of Li2CO3, Nb 2O5, and TiO2. This sort of dielectric ceramics exhibits relatively high dielectric permittivity, high quality factor value, and temperature coefficient, which are obtained by sintering at 1,100°C. It has been observed that the fired densities of the LNT ceramics increase with increasing sintering temperature, reach a maximum value as the sintering temperature is 1,100°C, then decrease slightly. The dielectric constant also first increases, reached the peak, and then decreased slightly with increasing sintering temperature.

Microwave dielectric properties of the 5.7Li 2 O–Nb 2 O 5 –7.3TiO 2 ceramics