Abstract:Vanadium oxynitride (VN x O y , x+y=1) is a metallic compound between vanadium oxides (VO, V 2 O 3 , V 2 O 5 ) and vanadium nitride (VN) which would have interesting properties and functions that potentially can be supplied for different applications. In this study, vanadium nitride and oxynitride thin films were obtained by reactive magnetron sputtering using vanadium targets, Ar as plasma carrier, and a mix of N 2 and O 2 as reactive gas. The ratio of mass flow between the two gases is maintained around O 2 :N 2 =1:20 during the process. To obtain crystalline phases of oxynitrides a post rapid thermal annealing (RTP) in Ar atmosphere at 600oC and 700oC for 5 minutes was done. The purpose of the study is to define the effect of the magnetron sputtering parameters, such as reactive gas flow rates, and annealing temperature on the composition, microstructure, and optical properties of the obtained vanadium oxynitride thin films. The characterization of obtained films includes the examination of thickness and morphology by the surface profiler and SEM; identifying crystal structures and further microstructural vibration modes of molecular polarizability by X-ray diffraction and Raman spectroscopy, respectively; evaluation of the chemical composition of films by XPS analysis; assessing of optical transmittance, reflectance, and absorbance by the UV-visible- NIR spectrometer. Experimental data reveal that the annealed films can be oxynitrides when the oxygen flow rate is below 0.25 sccm and the ratio of oxygen/nitrogen ≤1/20. The annealed vanadium oxynitride films in terms of their properties are closer to vanadium nitrides than to oxides: more metallic than semi-conductive with dark appurtenance and high optical absorbance across the spectrum between 200 and 900 nm. The optical absorbance reaches almost 90% around 300 nm and then slowly reduces to 70% at 900 nm. Thus, these films could be good optical shields. For practical usage, the deposition of O 2 :N 2 =1/20, O 2 <0.25 sccm, and 600oC annealing are recommended because of the truly low transmittance (<10%) through films.

Atomic Layer Deposition of Vanadium Oxide Thin Films from Tetrakis(dimethylamino)vanadium Precursor

Atomic Layer Deposition of Vanadium Dioxide and a Temperature-dependent Optical Model

Thermochromatic vanadium dioxide (VO2) thin films synthesized by atomic layer deposition and post-treatments

Atomic Layer Deposition Synthesis of thin Films of Vanadium Oxides in a Reducing Hydrogen Atmosphere

Effect of Vanadium Thickness and Deposition Temperature on VO2 Synthesis using Atmospheric Pressure Thermal Oxidation

Anodic Deposition of Vanadium Oxides for Thermal-Induced Growth of Vanadium Oxide Nanowires

Properties in Vanadium Dioxide Thin Film Synthesized from V2o5 Annealed in H-2/Ar Ambience

Fabrication of smooth thin film of vanadium oxides ($$\hbox {VO}_x$$) using pulsed laser deposition

V6O13films by Control of the Oxidation State from Aqueous Precursor to Crystalline Phase

Effect of Temperature on the Growth of Vanadium Oxide Films Deposited by DC Reactive Magnetron Sputtering

Synthesis and Properties of Vanadium Oxide Nanocoatings on the Surface of Polycrystalline α-Al2O3

Optical and electrical properties of vanadium oxides synthesized from alkoxides

Effect of vanadium precursor on dip-coated vanadium oxide thin films

Effect Of Annealing Processes On Composition And Thermal-Sensitive Properties Of Vanadium Oxide Thin Films

Study of Preparation and Characteristics Optimization of VO2 (B) Thin Films

Growth and thermal stability of (V,Al)2Cx thin films

Preparation and Characteristics of Vanadium Oxide Thin Films by Controlling the Sputtering Voltage

Vanadium Dioxide by Atomic Layer Deposition: A Promising Material for Next-Generation Memory Devices

(Digital Presentation) Fabrication and Characterization for Vanadium Oxynitride Thin Films By Magnetron Sputtering

Vanadium Dioxide Thin Films Synthesized Using Low Thermal Budget Atmospheric Oxidation

Growth, Electrical, and Optical Properties of Nanocrystalline Vo2 (011) Thin Films Prepared by Thermal Oxidation of Magnetron Sputtered Vanadium Films