Abstract:Cold-rolled AZ31 Mg alloy strips, with a reduction of 33 pct, were subjected to electropulse treatment (EPT) and conventional heat treatment (HT) to evaluate the respective influences of electropulses and temperature on the recrystallization behavior of AZ31. The highest measured temperature during the EPT (543 K) was used in HT. The electron backscattered diffraction results demonstrated that the EPT-stimulated recrystallization was completed within 8 seconds, whereas for HT, recrystallization was still far from completion even after 240 seconds. It was found that both the nucleation and grain growth of these two processes were totally different. In the EPT samples, nucleation tended to occur preferentially near extension twin boundaries and grain boundaries by continuous recrystallization, whereas in the HT samples, nucleation occurred mainly by grain boundaries bulging via discontinuous recrystallization. As grain growth proceeded, the texture intensities of the EPT samples decreased gradually and finally evolved into an obvious transverse-direction-split texture. This is likely attributable to the impact of electropulses on the boundary energy and the contribution of nonbasal dislocations; however, the basal-type textures of the HT samples were notably strengthened, which is associated with a 30 deg〈0001〉 orientation with respect to the deformed texture.

Texture Modification of Magnesium Alloys During Electropulse Treatment

Microstructure and Texture Evolution of Magnesium Alloys During Electropulse Treatment

Microstructure and texture evolution of cold-rolled Mg-3Al-1Zn alloy by electropulse treatment stimulating recrystallization

Texture Evolution in Cold-Rolled AZ31 Magnesium Alloy During Electropulsing Treatment

Microstructure and texture evolution of the cold-rolled AZ91 magnesium alloy strip under electropulsing treatment

On the Texture Weakening During Electropulse Annealing Treatment of Mg-1Ce Alloy: the Role of Nucleation and Nucleus Growth

Abnormal Texture Development in Magnesium Alloy Mg–3Al–1Zn During Large Strain Electroplastic Rolling: Effect of Pulsed Electric Current

Mechanism of Electropulsing Induced Recrystallization in a Cold-Rolled Mg–9Al–1Zn Alloy

A Comparative Study on the Static Recrystallization Behavior of Cold-Rolled Mg-3Al-1Zn Alloy Stimulated by Electropulse Treatment and Conventional Heat Treatment

Influence of Electropulsing Treatment on Microstructure and Mechanical Properties of Cold-Rolled Mg–9Al–1Zn Alloy Strip

Microstructure and Mechanical Properties of Cold-Rolled Mg-6Al-1Zn Alloy Strip Treated by Electropulsing Treatment

Enhancement of Ductility in Mg-3Al-1Zn Alloy with Tilted Basal Texture by Electropulsing

Improved mechanical properties of Mg-1Gd alloy by cold rolling and electropulse treatment

Microstructure and Texture Evolution of Mg-3Zn-1Al Magnesium Alloy During Large-Strain Electroplastic Rolling

Non-Basal Slip Induced Rare Earth Texture Evolution in Mg-14Gd-0.5Zr (wt.%) Alloy During the Traditional Hot Rolling

Effect of Electroplastic Treatment on Microstructure and Texture Changes of a Cold Rolling AZ31 Strip

Quasi-in-situ Observing the Rare Earth Texture Evolution in an Extruded Mg-Zn-Gd Alloy with Bimodal Microstructure

Deformation mechanisms and recrystallization behavior of Mg-3Al-1Zn and Mg-1Gd alloys deformed by electroplastic-asymmetric rolling

The Preferential Growth and Related Textural Evolution During Static Recrystallization in a Cold-Rolled Mg–Zn–Gd Alloy

Electropulsing Induced Texture Evolution in the Recrystallization of Fe-3 Pct Si Alloy Strip

Properties, microstructure and texture evolution of cold rolled Cu strips under electropulsing treatment