Abstract:Cold-rolled AZ31 Mg alloy strips, with a reduction of 33 pct, were subjected to electropulse treatment (EPT) and conventional heat treatment (HT) to evaluate the respective influences of electropulses and temperature on the recrystallization behavior of AZ31. The highest measured temperature during the EPT (543 K) was used in HT. The electron backscattered diffraction results demonstrated that the EPT-stimulated recrystallization was completed within 8 seconds, whereas for HT, recrystallization was still far from completion even after 240 seconds. It was found that both the nucleation and grain growth of these two processes were totally different. In the EPT samples, nucleation tended to occur preferentially near extension twin boundaries and grain boundaries by continuous recrystallization, whereas in the HT samples, nucleation occurred mainly by grain boundaries bulging via discontinuous recrystallization. As grain growth proceeded, the texture intensities of the EPT samples decreased gradually and finally evolved into an obvious transverse-direction-split texture. This is likely attributable to the impact of electropulses on the boundary energy and the contribution of nonbasal dislocations; however, the basal-type textures of the HT samples were notably strengthened, which is associated with a 30 deg〈0001〉 orientation with respect to the deformed texture.

Microstructure and texture evolution of the cold-rolled AZ91 magnesium alloy strip under electropulsing treatment

Microstructure and Texture Evolution of Magnesium Alloys During Electropulse Treatment

Texture Evolution in Cold-Rolled AZ31 Magnesium Alloy During Electropulsing Treatment

Influence of Electropulsing Treatment on Microstructure and Mechanical Properties of Cold-Rolled Mg–9Al–1Zn Alloy Strip

Microstructure and texture evolution of cold-rolled Mg-3Al-1Zn alloy by electropulse treatment stimulating recrystallization

Microstructure and Mechanical Properties of Cold-Rolled Mg-6Al-1Zn Alloy Strip Treated by Electropulsing Treatment

Effect of Electroplastic Treatment on Microstructure and Texture Changes of a Cold Rolling AZ31 Strip

Mechanism of Electropulsing Induced Recrystallization in a Cold-Rolled Mg–9Al–1Zn Alloy

Texture Modification of Magnesium Alloys During Electropulse Treatment

Enhancement of Ductility in Mg-3Al-1Zn Alloy with Tilted Basal Texture by Electropulsing

A Comparative Study on the Static Recrystallization Behavior of Cold-Rolled Mg-3Al-1Zn Alloy Stimulated by Electropulse Treatment and Conventional Heat Treatment

Effect of Electropulsing Treatment on Solid Solution Behavior of an Aged Mg Alloy AZ61 Strip

Properties, microstructure and texture evolution of cold rolled Cu strips under electropulsing treatment

Static Electropulsing-Induced Microstructural Changes and Their Effect on the Ultra-Precision Machining of Cold-Rolled AZ91 Alloy

Effect of Electropulsing Treatment on Microstructure and Tensile Fracture Behavior of Aged Mg–9Al–1Zn Alloy Strip

Effect of electropulsing treatment on the recovery of AZ31B magnesium alloy

Influence of Electropulsing Treatment on the Recrystallization and Texture of Ni9W Alloy Strip

Improved Ductility of Aged Mg-9Al-1Zn Alloy Strip by Electropulsing Treatment

Accumulation and Annihilation Effects of Electropulsing on Dynamic Recrystallization in Magnesium Alloy

Enhancement of Ductility, Weakening of Anisotropy Behavior and Local Recrystallization in Cold-Rolled Ti-6Al-4V Alloy Strips by High-Density Electropulsing Treatment

The Recovery Behavior of AZ31B Magnesium Alloy Stimulated by Electropulsing Treatment and Heat Treatment