Abstract:The symmetrical optical waveguide structures are fabricated in Er3+-doped aluminosilicate glass using 800 nm femtosecond laser writing in kHz repetition frequency regime. The impact of writing parameters on the waveguide preparation with a 10× microscope objective in the longitudinal writing scheme was studied in detail. The experimental results show that, under a fixed pulse energy value of 20 μJ, the waveguides can be realized with the scan speed from 20 to 160 μm/s, and with a fixed scan speed value of 160 μm/s, the waveguide can be prepared under an inscription energy range of 5–30 μJ, indicating that the waveguide can be realized in a wide range of writing parameters. The near-field mode intensity image shows that the waveguide region possesses excellent light guiding properties. Based on the refractive index profile reconstruction method, the maximum refractive index increase in the waveguide region is estimated to be about 5.5 × 10–4. The lowest propagation loss of the waveguide was measured to be about 1.51 dB/cm by the waveguide side scattering method. The microfluorescence spectra show that the gain characteristics of the waveguide region are well maintained after laser processing. This work shows that the fabrication of embedded optical waveguides using ultrashort pulse laser in Er3+-doped aluminosilicate glass has strong feasibility and great potential to create active gain devices in the field of integrated photonics and all-optical communication.

Transmission Performance of 90°-Bend Optical Waveguides Fabricated in Fused Silica by Femtosecond Laser Inscription.

Waveguide Bends from Nanometric Silica Wires

Optical loss measurements in femtosecond laser written waveguides in glass

Subwavelength-diameter Silica Wire for Light In-Coupling to Silicon-Based Waveguide

Fabrication of Optical Cavities with Femtosecond Laser Pulses

Effectively Writing Low Propagation and Bend Loss Waveguides in the Silica Glass by Using a Femtosecond Laser.

Suppression of bend loss in writing of three-dimensional optical waveguides with femtosecond laser pulses

Bending 90° Waveguides in Nd:YAG Crystal Fabricated by a Combination of Femtosecond Laser Inscription and Precise Diamond Blade Dicing

Transverse Writing of Multimode Interference Waveguides Inside Silica Glass by Femtosecond Laser Pulses

Low-loss optofluidic waveguides in fused silica enabled by spatially shaped femtosecond laser assisted etching combined with carbon dioxide laser irradiation

Direct Writing of Channel Optical Waveguides in Er 3+ -Doped Aluminosilicate Glass by Low Repetition Rate Femtosecond Laser

Femtosecond Laser Modification of Silica Optical Waveguides for Potential Bragg Gratings Sensing

New channel guiding structures via femtosecond laser direct writing z-cut LiNbO 3 crystals

Femtosecond laser written low-loss multiscan waveguides in fused silica

Optical Waveguide Writing Inside Foturan Glass with Femtosecond Laser Pulses

Silicon-on-Insulator Waveguide Devices for Broadband Mid-Infrared Photonics

Mid-infrared Nonlinear Silicon Hybrid Waveguide with High Figure of Merit

Femtosecond laser writing low-loss waveguides in silica glass: highly symmetrical mode field and mechanism of refractive index change

The structural and refractive index changes in the waveguides written by femtosecond laser in Er-doped silicate glasses

Fabrication of beam shapers in the bulk of fused silica by femtosecond laser pulses.

Single-step fabrication of surface waveguides in fused silica with few-cycle laser pulses