Abstract:The corrosion resistance and discharge activity of the rolled A represents aluminum, Z represents zinc, 9 and 1 represent their respective contents of 9% and 1% in the alloy magnesium alloy after electric pulse treatment show obvious patterns. Through research on its patterns and causes through immersion weight loss and electrochemical testing combined with microstructure observation results, it is found that the β‐Mg17Al12 phase and high‐energy grain boundary area in the alloy play a key role. In this article, a systematic investigation into the corrosion and discharge behaviors of as‐rolled a represents aluminum, Z represents zinc, 9 and 1 represent their respective contents of 9% and 1% in the alloy (AZ91) magnesium alloy after electro pulsing treatment (EPT), considering rolling deformations of 0% (as‐cast AZ91 magnesium alloy), 20%, 30%, and 40%, is presented. In this investigation, immersion weight loss tests, electrochemical tests, and other experimental methods are employed. In the results, it is revealed that the content of the β‐Mg17Al12 phase gradually decreases with increasing rolling deformation after EPT. Notably, the highest content of β‐Mg17Al12 phase and the most outstanding corrosion resistance are achieved with as‐cast AZ91 magnesium alloy. Furthermore, at low current densities (5 and 10 mA cm−2), the 30% rolling deformation exhibits superior discharge activity, while the discharge activity of the 40% rolling deformation is most excellent at high current densities (40 and 50 mA cm−2). The microstructure observations support these findings, highlighting the close relationship between the corrosion resistance and discharge activity of as‐rolled AZ91 magnesium alloy after EPT, and the content of the β‐Mg17Al12 phase and the area of high‐energy grain boundaries.

Improved Mechanical Properties of Mg–9Al–1Zn Alloy by the Combination of Aging, Cold-Rolling and Electropulsing Treatment

Improved Ductility of Aged Mg-9Al-1Zn Alloy Strip by Electropulsing Treatment

Microstructure and Mechanical Properties of Cold-Rolled Mg-6Al-1Zn Alloy Strip Treated by Electropulsing Treatment

Influence of Electropulsing Treatment on Microstructure and Mechanical Properties of Cold-Rolled Mg–9Al–1Zn Alloy Strip

Improved mechanical properties of Mg-1Gd alloy by cold rolling and electropulse treatment

Effect of Electropulsing Treatment on Microstructure and Tensile Fracture Behavior of Aged Mg–9Al–1Zn Alloy Strip

Microstructure and Tensile Properties of AZ61 Alloy Sheets Processed by High-Ratio Extrusion with Subsequent Direct Aging Treatment

Enhancement of Ductility in Mg-3Al-1Zn Alloy with Tilted Basal Texture by Electropulsing

Improved Plasticity of Mg–Al–Zn Alloy by Electropulsing Tension

Enhancing mechanical properties and corrosion resistance of a high strength 7A99 Al alloy by introducing pre-rolling in solution and aging treatments

Microstructure and texture evolution of the cold-rolled AZ91 magnesium alloy strip under electropulsing treatment

Mechanical Properties and Microstructures of Mg-Al-Zn Alloys with High Aluminum Contents

Achieving single-pass high-reduction rolling and enhanced mechanical properties of AZ91 alloy by RD-ECAP pre-processing

Accelerated solid solution and aging induced by electropulsing in Mg-Al-Ca-Mn alloy

Microstructure and texture evolution of cold-rolled Mg-3Al-1Zn alloy by electropulse treatment stimulating recrystallization

Corrosion and Discharge Behavior of As‐Rolled AZ91 Magnesium Alloy after Electro‐Pulsing Treatment

Pre-precipitating promoted by microshear bands effectively circumvents strength-ductility trade-off of RT-rolled Al–6Zn–1Mg alloy

An alternating ageing-annealing process for enhancing strength and ductility of a Mg-Gd-Y-Zn-Zr alloy

Response of mechanical properties and corrosion behavior of Al–Zn–Mg alloy treated by aging and annealing: A comparative study

Mechanism of Electropulsing Induced Recrystallization in a Cold-Rolled Mg–9Al–1Zn Alloy

Improving the mechanical properties of duplex Mg-Li-Zn alloy by mixed rolling processing