Research on hot isostatic pressing sintering behavior of 90W–Ni–Fe–Cu alloy
Jianning Wang,Wensheng Liu,Yunzhu Ma,Wentan Zhu,Baishan Chen,Lei Zhang,Kuokuo Bao,Chaoping Liang,Qingshan Cai
DOI: https://doi.org/10.1016/j.jmrt.2023.09.053
IF: 6.267
2023-09-21
Journal of Materials Research and Technology
Abstract:In order to understand the underlying material evolution during liquid phase sintering (LPS) process in hot isostatic pressing process (HIP), microstructure and mechanical properties of 90 W–Ni–Fe–Cu alloys fabricated at 1400 °C/150 MPa are examined systematically. For 90W-4.2Ni-1.8Fe–4Cu alloy, the typical LPS microstructure, which are spherical W grains uniformly surrounded by continuously distributed γ- (Ni, Fe, Cu) matrix phase with the lowest W–W contiguity of 0.31, is achieved successfully after HIP at 1400 °C/150 MPa. The excellent tensile strength reaches as high as 873 MPa with elongation of 17.3% due to the soft γ- (Ni, Fe, Cu) matrix phase. Moreover, the relationship between the microstructure parameters VM(1−CW−W) and elongation ε are established and analyze the association with dislocation motion in depth through electron backscattered diffraction (EBSD) characterization. To our best knowledge, the LPS behavior of tungsten alloy is in-situ revealed by high-temperature confocal scanning laser microscopy (HT-CSLM) for the first time. The current research provides a novel strategy for designing and fabricating powder metallurgy materials by LPS with pressure.
materials science, multidisciplinary,metallurgy & metallurgical engineering