Microstructure and high-temperature mechanical properties of near net shaped Ti−45Al−7Nb−0.3W alloy by hot isostatic pressing process

Hui-zhong LI,Yi-xuan CHE,Xiao-peng LIANG,TAO Hui,Qiang ZHANG,Fei-hu CHEN,HAN Shuo,LIU Bin,Hui TAO,Shuo HAN,Bin LIU
DOI: https://doi.org/10.1016/s1003-6326(20)65438-3
IF: 3.752
2020-11-01
Transactions of Nonferrous Metals Society of China
Abstract:Near net shaped Ti−45Al−7Nb−0.3W alloy (at.%) parts were manufactured by hot isostatic pressing (HIP). The microstructure and high-temperature mechanical properties of the alloy were investigated by X-ray diffractometry (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The results show that at a temperature of 700 °C, the peak yield stress (YS) and ultimate tensile stress (UTS) of alloy are 534 and 575 MPa, respectively, and the alloy shows satisfactory comprehensive mechanical properties at 850 °C. The alloy exhibits superplastic characteristics at 1000 °C with an initial strain rate of 5×10<sup>−5</sup> s<sup>−1</sup>. When the tensile temperature is below 750 °C, the deformation mechanisms are dislocation movements and mechanical twinning. Increasing the tensile temperature above 800 °C, grain boundary sliding and grain rotation occur more frequently due to the accumulation of dislocations at grain boundary.
metallurgy & metallurgical engineering
What problem does this paper attempt to address?
This paper aims to study the microstructure and high - temperature mechanical properties of near - net - shape Ti−45Al−7Nb−0.3W alloy fabricated by the Hot Isostatic Pressing (HIP) process. Specifically, the paper focuses on the following points: 1. **Microstructure analysis**: The microstructure characteristics of the alloy at different temperatures were analyzed by means of X - ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). 2. **High - temperature mechanical properties**: The tensile properties of the alloy at different initial strain rates in the range of 20°C to 1000°C were studied, including yield strength (YS), ultimate tensile strength (UTS) and elongation. 3. **Deformation mechanism**: The deformation mechanisms of the alloy at different temperatures were explored, especially the differences below and above the eutectoid temperature. Specifically, the paper analyzed the influence of mechanisms such as dislocation movement, mechanical twinning, grain boundary sliding and grain rotation on the properties of the alloy. ### Main findings - **Room temperature to 700°C**: As the temperature increases, the yield strength and ultimate tensile strength of the alloy first decrease and then increase, reaching a peak at 700°C (YS = 534 MPa, UTS = 575 MPa). At this time, the alloy exhibits an abnormal strengthening phenomenon. As the temperature continues to rise, the yield strength and ultimate tensile strength decrease again, but the elongation continues to increase. - **850°C**: The alloy exhibits good comprehensive mechanical properties at 850°C, with a yield strength of 351 MPa, an ultimate tensile strength of 390 MPa and an elongation of 67%. - **1000°C**: The alloy exhibits superplastic deformation characteristics at 1000°C, with an elongation as high as 141%. At this time, grain boundary sliding becomes the main deformation mechanism, the dislocation density is significantly reduced, and the grain boundary sliding promotes the rapid decrease of the flow stress, thereby increasing the elongation. ### Deformation mechanism - **Below 700°C**: The main deformation mechanisms are dislocation movement and mechanical twinning. - **Above 850°C**: The main deformation mechanisms are dislocation movement, mechanical twinning, grain boundary sliding and rotation of the α2/γ lamellar structure. ### Conclusions 1. The alloy exhibits the highest ultimate tensile strength and good elongation at 700°C. 2. At 850°C, the alloy has the best comprehensive mechanical properties. 3. The alloy exhibits superplastic deformation characteristics at 1000°C, and the main deformation mechanisms are grain boundary sliding and grain rotation. Through these studies, the paper provides important scientific basis and technical support for understanding and optimizing the high - temperature mechanical properties of TiAl - based alloys.