Microstructures and tensile properties of Ti₂AlNb and Mo-modified Ti₂AlNb alloys fabricated by hot isostatic pressing

Yaran Zhang,Yongchang Liu,Liming Yu,Hongyan Liang,Yuan Huang,Zongqing Ma

DOI: https://doi.org/10.1016/j.msea.2020.139043

2020-01-01

Abstract:The Ti2AlNb and Mo-modified Ti2AlNb alloys were fabricated by hot isostatic pressing, and then underwent annealing treatment at 800 degrees C for 1, 2 and 3 h respectively. To evaluate the tensile properties of the two kinds of alloys, tensile tests were conducted at ambient temperature and 650 degrees C in this study. For the Ti2AlNb alloy, the room-temperature ultimate tensile strength (UTS) was 700-900 MPa, and the highest elongation to failure (epsilon(f)) reached 6.2% after aging for 2 hat 800 degrees C. Since the Mo addition promoted the precipitation of the coarse B2+O colony structure near the grain boundary, the Mo-modified Ti2AlNb alloy exhibited decreased UTS and epsilon(f) at room temperature. As for the high-temperature performance of both the Ti2AlNb and Mo-modified Ti2AlNb alloys, the UTS reached approximately 700 MPa and the epsilon(f) exceeded 3.0%. Meanwhile, the two kinds of alloys presented the same tendency that both the high-temperature UTS and epsilon(f) increased firstly and then decreased as the aging time increased. Among them the specimens after aging at 800 degrees C for 2 h for both alloys acquired the highest UTS and epsilon(f). Moreover, the Mo-modified alloy exhibited a better high-temperature ductility than that at room temperature, which is associated with the B2 <-> O phase transformation during the loading at 650 degrees C. The Mo addition effectively refined the lath of the precipitates in the grain and the grain size of the matrix, and it induced abundant dislocations. Thus, the Mo-modified Ti2AlNb alloy aged for 1 and 3 h exhibited superior high-temperature mechanical properties than those of the Ti2AlNb alloy.