Abstract:Poly(lactide-co-glycolide) (PLGA) copolymers are the most prevalent materials for tissue engineering applications. To mimic the real microenvironment of extracellular matrix (ECM) for cell growth, nanofibrous PLGA scaffolds are preferred. PLGA5050 (in which the molar ratio of lactidyl to glycolidyl units is 50:50), which is an utterly amorphous polymer, was first reported to be made into nanofibrous networks (fiber diameter around 500nm) using phase separation from PLGA5050/THF solutions in this study. The concentration of polymeric solution had significant effects on fiber diameter and unit length. Nonsolvent (e.g. H2O) was unnecessary to form the PLGA5050 gel, which was critical to nanofibrosis, as if the environmental temperature for gelation occurrence was low enough (−70°C). The physical crosslinks to stabilize the PLGA5050/THF gel were believed to be GA segments along the backbone owing to their inferior solubility in THF. The addition of H2O would cause adverse effects of liquid–liquid phase separation and nanofibrosis failure owing to the hydrophilicity of glycolidyl units. Associating with the phase separation method, particle-leaching technique was applied to fabricate three-dimensional scaffolds with macroporous and nanofibrous structures. To ensure the occurrence of nanofibrosis on macropore walls, the temperature of salt particles should be best lowed to −70°C beforehand. Accordingly, scaffolds prepared under varied parameters exhibited different nanofiber and pore morphologies, which affected the pore size, porosity, specific surface area, water contact angle and protein adsorption ability etc. The preliminary cell (MC3T3-E1) culture confirmed the cell ingrowth into the macroporous and nanofibrous PLGA5050 scaffolds in comparison with the solely nanofibrous matrixes. This kind of bi-scaled three dimensional matrixes can be superior candidate scaffolds for tissue engineering applications.

The Crystallization Behavior of Porous Poly(lactic Acid) Prepared by Modified Solvent Casting/particulate Leaching Technique for Potential Use of Tissue Engineering Scaffold

Preparation of Highly Porous Interconnected Poly(Lactic Acid) Scaffolds Based on A Novel Dynamic Elongational Flow Procedure

Ultraporous Poly(Lactic Acid) Scaffolds With Improved Mechanical Performance Using High-Pressure Molding And Salt Leaching

Preparation of Porous Poly (L-Lactic Acid) (PLLA) Scaffold by Porogen Leaching and Freeze Drying

Porous polymeric structures for tissue engineering prepared by a coagulation, compression moulding and salt leaching technique

Engineering Porous Poly(lactic Acid) Scaffolds with High Mechanical Performance Via a Solid State Extrusion/Porogen Leaching Approach

Microstructural Characteristics And Crystallization Behaviors Of Poly(L-Lactide) Scaffolds By Thermally Induced Phase Separation

Formation of Porous PLGA Scaffolds by a Combining Method of Thermally Induced Phase Separation and Porogen Leaching

Effect of Mixed Solvents on the Thermal Properties of Poly(l-Lactic Acid) (PLLA) Solution and Micromorphology of Porous PLLA Scaffolds

High-performance Porous Polylactide Stereocomplex Crystallite Scaffolds Prepared by Solution Blending and Salt Leaching.

Impact of foaming air on melting and crystallization behaviors of microporous PLA scaffolds

Characterization of Highly Interconnected Porous Poly(lactic Acid) and Chitosan-Coated Poly(lactic Acid) Scaffold Fabricated by Vacuum-Assisted Resin Transfer Molding and Particle Leaching

Facile Preparation of Open-Cellular Porous Poly (L-Lactic Acid) Scaffold by Supercritical Carbon Dioxide Foaming. for Potential Tissue Engineering Applications

Particle-collision and Porogen-Leaching Technique to Fabricate Polymeric Porous Scaffolds with Microscale Roughness of Interior Surfaces

Microstructure and Mechanical Properties of Poly(l‐lactide) Scaffolds Fabricated by Gelatin Particle Leaching Method

Preparation of Porous Polycaprolactone Scaffolds by Using Freeze-Drying Combined Porogen-Leaching Methods

Specially Elaborated Thermally Induced Phase Separation to Fabricate Poly(L-Lactic Acid) Scaffolds with Ultra Large Pores and Good Interconnectivity

Toward Biomimetic Porous Poly(ε-Caprolactone) Scaffolds: Structural Evolution and Morphological Control During Solid Phase Extrusion

Study on poly(ε-caprolactone) scaffolds with multi-model pores through phase separation/salt leaching process

Macroporous and nanofibrous poly(lactide-co-glycolide)(50/50) scaffolds via phase separation combined with particle-leaching

Study on fabrication of poly(lactic acid) porous scaffolds