Study on Preparation and Morphology Structure of PLLA Cell Scaffold

CUI Wenjin,TU Chifeng,BEI Jianzhong,WANG Shenguo

DOI: https://doi.org/10.3969/j.issn.1673-0364.2005.06.007

2005-01-01

Abstract:Objective To prepare PLLA cell scaffold with three different processing and study the effect of the processing on pore structure of cell scaffold. Methods The PLLA scaffolds were fabricated by solution casting/porogen leaching method, solid-liquid phase separation method and liquid-liquid phase separation method. The porosity and average pore diameter of the PLLA scaffold were measured and microstructure of the scaffolds was observed. Results The porosity and pore size of the scaffold prepared with solution casting/porogen leaching method can be adjusted by changing the porogen content and the porogen size. A new technique of fabricating scaffold was devised by combining the porogen-leaching method with solid-liquid phase separation to obtain the scaffold with pore diameter over 200μm and good pore interconnectivity. The pore diameter of the scaffold was regulated by the phase separation parameters during liquid-liquid phase separation. The biggest pore diameter of the scaffold reach 360μm under the optimum phase separation conditions, which exceeded the common diameter (120μm ) of the scaffold reported in the reference. Conclusions The PLLA cell scaffolds with requiring porosity and pore size to use in tissue engineering were obtained by above described three different processing. Only flat sheets scaffold can be formed by the solution casting/porogen leaching method, but other more complex shape can be obtained by phase separation method.