Abstract:Poly(lactide-co-glycolide) (PLGA) copolymers are the most prevalent materials for tissue engineering applications. To mimic the real microenvironment of extracellular matrix (ECM) for cell growth, nanofibrous PLGA scaffolds are preferred. PLGA5050 (in which the molar ratio of lactidyl to glycolidyl units is 50:50), which is an utterly amorphous polymer, was first reported to be made into nanofibrous networks (fiber diameter around 500nm) using phase separation from PLGA5050/THF solutions in this study. The concentration of polymeric solution had significant effects on fiber diameter and unit length. Nonsolvent (e.g. H2O) was unnecessary to form the PLGA5050 gel, which was critical to nanofibrosis, as if the environmental temperature for gelation occurrence was low enough (−70°C). The physical crosslinks to stabilize the PLGA5050/THF gel were believed to be GA segments along the backbone owing to their inferior solubility in THF. The addition of H2O would cause adverse effects of liquid–liquid phase separation and nanofibrosis failure owing to the hydrophilicity of glycolidyl units. Associating with the phase separation method, particle-leaching technique was applied to fabricate three-dimensional scaffolds with macroporous and nanofibrous structures. To ensure the occurrence of nanofibrosis on macropore walls, the temperature of salt particles should be best lowed to −70°C beforehand. Accordingly, scaffolds prepared under varied parameters exhibited different nanofiber and pore morphologies, which affected the pore size, porosity, specific surface area, water contact angle and protein adsorption ability etc. The preliminary cell (MC3T3-E1) culture confirmed the cell ingrowth into the macroporous and nanofibrous PLGA5050 scaffolds in comparison with the solely nanofibrous matrixes. This kind of bi-scaled three dimensional matrixes can be superior candidate scaffolds for tissue engineering applications.

Manufacturing and morphology structure of polylactide-type microtubules orientation-structured scaffolds.

Fabrication of a tubular vascular scaffold with circumferential microchannels to induce oriented growth of smooth muscle cells

Microfabrication of 3D-Polymeric Structures Using Soft Lithography for Tissue Engineering

Structural mechanics of 3D-printed poly(lactic acid) scaffolds with tetragonal, hexagonal and wheel-like designs.

Porous Morphology and Mechanical Properties of Poly(lactide-Co-glycolide) Hollow Fiber Membranes Governed by Ternary-Phase Inversion

Macroporous and nanofibrous poly(lactide-co-glycolide)(50/50) scaffolds via phase separation combined with particle-leaching

Specially Elaborated Thermally Induced Phase Separation to Fabricate Poly(L-Lactic Acid) Scaffolds with Ultra Large Pores and Good Interconnectivity

Novel Airflow-Field-Driven Melt Spinning 3D Printing of Tubular Scaffolds Based on Polycaprolactone Blends

Fabrication of three dimensional polymeric scaffolds with spherical pores

Fabrication of Three-Dimensional Porous Scaffolds of Complicated Shape for Tissue Engineering. I. Compression Molding Based on Flexible-Rigid Combined Mold.

Microstructure and Mechanical Properties of Poly(l‐lactide) Scaffolds Fabricated by Gelatin Particle Leaching Method

A Novel Poly (Lactic-Co-Glycolic Acid)-Collagen Hybrid Scaffold Fabricated Via Multi-Nozzle Low-Temperature Deposition

Study on Preparation and Morphology Structure of PLLA Cell Scaffold

Polylactone-type Polymeric Microspheres Injectable Cell Scaffold

Porous Morphology, Porosity, Mechanical Properties Of Poly(Alpha-Hydroxy Acid)-Tricalcium Phosphate Composite Scaffolds Fabricated By Low-Temperature Deposition

Porous polymeric structures for tissue engineering prepared by a coagulation, compression moulding and salt leaching technique

Poly(L-Lactide) Melt Spun Fiber-Aligned Scaffolds Coated with Collagen or Chitosan for Guiding the Directional Migration of Osteoblasts in Vitro

Particle-collision and Porogen-Leaching Technique to Fabricate Polymeric Porous Scaffolds with Microscale Roughness of Interior Surfaces

Paraffin Spheres As Porogen to Fabricate Poly(L-Lactic Acid) Scaffolds with Improved Cytocompatibility for Cartilage Tissue Engineering

Fabrication and evaluation of 3D printed poly(l-lactide) copolymer scaffolds for bone tissue engineering

Manufacture and characteristics of HA-Electrodeposited polylactic acid/polyvinyl alcohol biodegradable braided scaffolds