Abstract:Using pyromelliticdianhydride (PMDA) and polyfunctional epoxy ether (PFE) as branching agent, long chain branching stereocomplex poly(L‐lactide)s and poly(D‐lactide)s was prepared by reactive processing, respectably. Then stereocomplex poly(lactide)s of long chain branching PLLA and PDLA (sc‐PLA/BA) was prepared by solution blending and its fabricated the vascular stents via 3D‐printing.The effects of branching structure on melt crystallization behavior of sc‐PLA/BA investigated by DSC. The influence of the branching agent content on the crystallization ability of samples shows a bell‐shaped relationship, there is a maximum point when the branching agent content is1.5 wt%. When the branching agent content is less than 1.5 wt%, the crystallization ability of the sample increased with the increasing of branching agent content. When the branching agent content exceeded than 1.5 wt%, the crystallization ability of the samples decreased with branching agent content increasing. Such behavior is as the linear PLA branched to dendrite configuration, the enrichment of segments around branching structure within branched chains promoted its nucleation. But the high degree of branching caused inter‐ or intrachians entanglement which obstructed the segments movement and growth into the crystals. The half‐time of crystallization (t1/2) of the samples decreased from 6 minutes for initial sc‐PLA/BA‐0 to 3 minutes of sc‐PLA/BA‐1.5 wt% at 163°C. POM results indicated that nucleation density of sc‐PLA/BA significantly increased with the branching agent increasing. Moreover, mechanical testing demonstrated that forming branching structure could be an effective modification of the mechanical properties for sc‐PLA, its tensile strength and modulus increases from 57.3 MPa and 2.02 GPa to 70.4 MPa and 3.31 GPa, respectively. TGA results analyzed by FWO method and Kissinger method, indicated the apparent activation energy of sc‐PLA/BA samples increases from 96.8 to 113.3 kJ/mol, suggesting the improvement of heat resistance. The CCK‐8 assay, ALP assay and cell Live/Dead assay results indicated that sc‐PLA with branching structure presented very low cell cytotoxicity. Therefore, the long chain branching sc‐PLA matrix with branching agent could effectively improve its crystallization abilities, mechanical properties, heat resistance and biocompatibilities.

Stereocomplex Poly(lactic Acid) Vascular Stents by 3d‐printing with Long Chain Branching Structures: Toward Desirable Crystallization Properties and Mechanical Performance

Competing Stereocomplexation and Homocrystallization of Poly(l-lactic Acid)/poly(d-Lactic Acid) Racemic Mixture: Effects of Miscible Blending with Other Polymers

Crystallization and Biocompatibility Enhancement of 3D-Printed Poly(l-Lactide) Vascular Stents with Long Chain Branching Structures

Introduction of Stereocomplex Crystallites of PLA for the Solid and Microcellular Poly(lactide)/poly(butylene Adipate-Co-terephthalate) Blends

Enhancement of the crystallization and biocompatibility of poly(TMC-b-(LLA-ran-GA)) by poly(lactide) stereocomplex

Enhanced Crystallization Rate and Mechanical Properties of Poly(l‐lactic Acid) by Stereocomplexation with Four‐armed Poly(ϵ‐caprolactone)‐block‐poly(d‐lactic Acid) Diblock Copolymer

Synergistic effect of star‐shaped architecture and polyethylene glycol moieties on poly (lactic acid) stereocomplex crystallization behaviors

Enhancing Crystallization Behavior for Optimized Performances of Poly(tmc‐b‐(lla‐ran‐ga)) by PDLA/PLLA Stereocomplex Crystallization

<scp>3D</scp> printed peripheral vascular stents based on degradable poly(<scp>trimethylene carbonate‐b‐(L‐lactide‐ran‐glycolide)</scp>) terpolymer

Synthesis and characterization of polylactides with different branched architectures

3D printed peripheral vascular stents based on degradable poly(trimethylene carbonate-b-(L-lactide-ran-glycolide)) terpolymer

Effect of Stereocomplexation on High-temperature Microcellular Foaming Behaviour, Compressive Property and Heat Resistance of Branched Poly(l-lactide)/poly(d-lactide)

Exclusive Stereocomplex Crystallization of Linear and Multiarm Star-Shaped High-Molecular-Weight Stereo Diblock Poly(lactic acid)s.

Influence of poly(lactide) stereocomplexes as nucleating agents on the crystallization behavior of poly(lactide)s

Crystallization, thermal and mechanical properties of stereocomplexed poly(lactide) with flexible PLLA/PCL multiblock copolymer

Regulating the Crystallization Behaviors of High-molecular-weight Poly(lactic acid) Stereocomplex System Based on the Structure of Poly(ethylene glycol)

Formation, structure and promoting crystallization capacity of stereocomplex crystallite network in the poly(lactide) blends based on linear PLLA and PDLA with different structures

The Preparation of Chain Branching PLLA by Intermolecular Hydrogen Bonding with 3-Pentadecylphenol and Its Crystallization, Relaxation Behavior and Thermal Stability

Shape memory properties of 3D‐printed self‐expandable poly(lactic acid) vascular stents with long‐chain branched structures

Stereocomplex-type Polylactide with Remarkably Enhanced Melt-Processability and Electrical Performance Via Incorporating Multifunctional Carbon Black

Enhancement of the properties of biodegradable poly(L-lactide)/poly(butylene carbonate) blends by introducing stereocomplex polylactide crystals