Abstract:In this paper, un-, Fe-, Ni- and (Fe + Ni)-doped ZnO layers were grown on transparent glass substrates by sol–gel process using the spin-coating technique. Investigations based on different techniques such as XRD, SEM, UV–visible spectroscopy, PL and VSM were performed to analyze the samples. X-ray diffraction (XRD) analysis revealed the formation of hexagonal structure corresponding to the wurtzite phase of all samples without any secondary phases present in the spectra. The average crystallite size is in 36–80 nm range. Scanning electron microscopy (SEM) investigation of the layers reveals that following doping, the ZnO grain sizes tend to increase. UV–visible shows red shift in peak wavelength. These findings are in line with the grain size dependence after doping obtained from XRD. Using transmittance spectra, the optical energy bandgap was found 3.29, 3.17, 3.11 and 3.15 eV of un-, Fe-, Ni- and (Ni + Fe)-doped ZnO, respectively. Un-doped ZnO has the highest intensity in near-band-edge emission, according to photoluminescence (PL) spectra, but after Ni and Fe doping, a slight redshift is observed with a strong violet (423 nm) and blue (475 nm) emission peaks, respectively. Hence, for Zn 1−2 x Ni x Fe x O ( x = 0.01 and 0.03 mol%) thin films, the ensuing emission properties make them appropriate as lighting sources. Consequently, it is anticipated that full-color display devices would be possible. Vibrating sample magnetometer (VSM) measurements at room temperature are discovered to be hysteretic, indicating room temperature ferromagnetism (RTFM) and implying the Curie temperature is greater than 300 K. The area under the hysteresis loop of Zn 1−2 x Ni x Fe x O ( x = 0.01 and 0.03 mol%) decreases, indicating low hysteresis loss. The present findings are suitable for spintronic applications.

Preparation of ZnO–B 2 O 3 –SiO 2 :Mn 2+ optical-storage glass–ceramics with different ZnF 2 dopant by sol–gel method

Effects of the replacing content of ZnBr 2 on the properties of ZnO–B 2 O 3 –SiO 2 :Mn 2+ glass-ceramics

Sol-gel preparation and phosphorescence property of Mn 2+ -doped zinc borosilicate glass thin films

Preparation and Characterization of Mg-doped ZnO Thin Films by Sol–gel Method

Microstructue and Optical Properties of Mg-doped ZnO Thin Films Prepared by Sol-gel Method

A Study of Formation and Photoluminescence Properties of ZnO Quantum Dot Doped Zinc-Alumino-silicate Glass Ceramic

Dielectric and energy storage properties of Bi 2 O 3 -B 2 O 3 -SiO 2 doped Ba 0.85 Ca 0.15 Zr 0.1 Ti 0.9 O 3 lead-free glass-ceramics

Effect of Samarium on Mn Activated Zinc Borosilicate Storage Glasses

Effect of Network-Forming Oxides on Long-Lasting Phosphorescencein Mn2+ Doped ZnO-B2O3-SiO2 Glass

Preparation of long-lasting phosphorescence (LLP) glass-ceramic materials

Effect of LMZBS Glass on the Microstructure and Microwave Dielectric Properties of Monocelsian Ceramics

Influence of Li<sub>2</sub>O-MgO-ZnO-B<sub>2</sub>O<sub>3</sub>-SiO<sub>2</sub>glass doping on the microwave dielectric properties and sintering temperature of Li<sub>3</sub>Mg<sub>2</sub>NbO<sub>6</sub>ceramics

Influence of Li2O–B2O3–SiO2 Glass on the Sintering Behavior and Microwave Dielectric Properties of BaO–0.15ZnO–4TiO2 Ceramics

Preparation and Optical Properties of Solid Solution Semiconductor (zn X Cd1−x S) Doped Silica Glasses

Investigation on Glass-Forming Ability,flexural Strength and Microwave Dielectric Properties of Al2O3-doped LMZBS Glasses

Luminescence properties and thermal stability of Dy2O3/Sm2O3 doped glass ceramics containing NaBi(WO4)2

Study of Zn1−2xNixFexO thin films coated on glass by sol–gel spin-coating method for DMS materials

Low-temperature sintering of (Zn0.8 Mg0.2)2SiO4–TiO2 ceramics

Densification Behavior and Dielectric Properties of CaO-B2O3-SiO2 System Glass-Ceramics Containing ZrO2

The Preparation and Microwave Properties of Ba3ZnZCo2-ZFe24O41/SiO2 Microcrystalline Glass Ceramics by Citrate Sol-Gel Process

Sintering Behavior and Microwave Dielectric Properties of LMZBS Glass Doped Li 3 Mg 4 NbO 8 Ceramics for LTCC Applications