Abstract:This study investigates the structure–property relationship in a dissimilar joint between super duplex stainless steel (sDSS 2507) and pipeline steel (X-70) using gas tungsten arc welding and ER2594 filler. Tubing and risers used to transport hydrocarbons are regularly joined using these dissimilar metals. The microstructures of lower heat input (LHI-0.7 kJ/mm) and higher heat input (HHI-1.4 kJ/mm) weldments were examined to understand the influence of heat input on the structure–property relationship. The weldments' mechanical characteristics were tested via hardness, impact, and tensile tests. Base metal and weld zone/interface characterization were studied utilizing optical and scanning electron microscopes with energy-dispersive spectroscopy (EDS). Elemental variation was confirmed by EDS spectra, elemental line mapping, and electron probe microanalysis with wavelength-dispersive spectrometer along the weld interface and weld zone. Significant microstructure variation was observed in X-70 BM at the LHI and HHI weld interfaces. Type II boundary and macro-segregation forms like peninsulas and islands were present in both weldments. In LHI and HHI weldment, duplex microstructure dominates the weld zone cap and filler pass. In the backing pass, duplex microstructure replaces skeletal ferrite, which predominates in the root pass of the HHI weld zone. LHI weldment has an average microhardness of 275 ± 7 HV 0.5 , while HHI had 285 ± 5 HV 0.5 . Both weldment's tensile tests revealed that the sample fractured on the weaker X70 BM side. LHI and HHI weldments had 600 MPa and 610 MPa ultimate tensile strengths and 22% and 18% elongation percentages, respectively. LHI weldments (200 ± 7 J, 210 ± 4 J) and HHI weldments (210 ± 5 J, 220 ± 8 J) have lower average impact toughness in cap and root pass than the sDSS 2507 BM (320 ± 3 J) and X-70 BM (300 ± 6 J), respectively. The increase in heat input led to a minimal 2% difference in tensile strength, a notable 10% increase in hardness, and a slight 5% variation in impact toughness between LHI and HHI weldments. Marine and offshore applications may benefit from investigating the sDSS 2507/X-70 DWJ's process parameter selection, thermodynamic analysis, and structure–property relationship.

Properties of X80 Pipeline Girth Welds for Different Welding Procedures

Correlation Between Heterogeneous Micromechanical Properties and Fracture Toughness in X80 Girth Weld

Research of Micro-Alloyed Microstructure and Composition in X80 Pipeline Steel for High Heat Input Welding

Effect of Microstructure on Mechanical Properties of X65MS Welded Pipe Joint

Simultaneously enhancing strength and fracture toughness via tailoring the microstructure in X80 girth weld metal

Comparison of Microstructures and Properties of X80 Pipeline Steel Additively Manufactured Based on Laser Welding with Filler Wire and Cold Metal Transfer

Changes in microstructure and properties of weld heat-affected zone of high-strength low-alloy steel

Effects of Quenching Cooling Rates on Microstructure and Properties of X80 Pipe Fitting Welds

Submerged Arc Welding Wire Matched with X80 Pipeline Steel

Microstructure and Property of Coarse Grain Haz X80 Pipeline Steel

FRACTURE TOUGHNESS OF WELDED JOINTS OF X100HIGH-STRENGTH PIPELINE STEEL

Structure–property relationship assessment of dissimilar gas tungsten arc welded joint of pipeline steel and super duplex stainless steel for marine applications

Microstructure and mechanical properties of X90 high strength pipeline steel

A comparative study of the microstructure and properties of 800 MPa microalloyed C-Mn steel welded joints by laser and gas metal arc welding

Coarse Grain Heat Affect Zone Microstructures and Toughness of X80 Pipeline Steel

Tempering Microstructure and Mechanical Properties of Pipeline Steel X80

Butt Welding of 2205/X65 Bimetallic Sheet and Study on the Inhomogeneity of the Properties of the Welded Joint

Microstructure and Mechanical Properties of the Ternary Gas Shielded Narrow-Gap GMA Welded Joint of High-Strength Steel

Fracture driving forces of cracked girth welds with mechanical heterogeneity for X80 pipes

Corrosion fatigue behavior of X65 pipeline steel welded joints prepared by CMT/GMAW backing process

Inhomogeneous Strain Behaviors of the High Strength Pipeline Girth Weld under Longitudinal Loading