Abstract:Brittle fracture of girth weld metal is the main failure form of high strength steel oil and gas pipeline facilities, which is related to the deterioration of mechanical properties of weld metal at low temperature, especially the fracture toughness. In order to improve the strength and fracture toughness, tempering and intercritical quenching-tempering treatment are used in X80 girth weld metal. The results demonstrate that the heat treatment processes not only decomposed M-A constituent, but also increased grain size, reduced dislocation density and increased precipitated phase content. In the intercritical quenching-tempering treatment, small size retained austenite was produced, which was rich in carbon and manganese elements. The tempering and intercritical quenching-tempering treatment process significantly improved the tensile properties and fracture toughness, so that the R t0.5 increased from 598 MPa to 629 MPa and 648 MPa, and the value of crack tip opening displacement (CTOD) increased from 0.05 mm to 0.12 mm and 0.23 mm, respectively. (Nb,Ti)C precipitated during heat treatment could effectively improve the yield strength, and the increase of precipitation strengthening is much higher than the strength loss caused by grain size increase and dislocation density reduction. Transformation induced plasticity effect of stable retained austenite formed by intercritical quenching-tempering treatment could effectively inhibit crack propagation and improve fracture toughness. The combined effect of retained austenite and nano-precipitated (Nb,Ti)C significantly improves the strength and fracture toughness of the weld metal. Generally, the research results have important scientific value and engineering significance for explaining the strength and toughness mechanism of girth weld and practical pipeline engineering application.

FRACTURE TOUGHNESS OF WELDED JOINTS OF X100HIGH-STRENGTH PIPELINE STEEL

Fracture Toughness Investigation of X100 Longitudinal Submerged Arc Welded Pipe Via Crack Tip Opening Displacement Test

Experiment on the Fracture Toughness of Weld Joint of X70 Pipeline Steel

Experimental Research on Fracture Toughness of High Grade Line Pipe

Changes in microstructure and properties of weld heat-affected zone of high-strength low-alloy steel

Crack Tip Opening Displacement of X100 Sawl Pipe

Improving the Weld Heat-Affected-Zone (HAZ) Toughness of High-Strength Thick-Walled Line Pipes

FRACTURE TOUGHNESS OF X70 PIPELINE STEEL AT DIFFERENT TEMPERATURES

Study on Fracture Behavior and Toughening Mechanisms of Ultra-High-Strength Pipeline Steel

Analysis on Microstructure and Impact Toughness of X100 and X80 Pipeline Steel

Simultaneously enhancing strength and fracture toughness via tailoring the microstructure in X80 girth weld metal

Correlation Between Heterogeneous Micromechanical Properties and Fracture Toughness in X80 Girth Weld

Coarse Grain Heat Affect Zone Microstructures and Toughness of X80 Pipeline Steel

Research on Microstructure and Performance in Welding HAZ of X100 SAWH Pipe

Relationship Between Microstructure and Mechanical Properties of X100 Pipeline Steel

Effect of root welding heat input on microstructure evolution and fracture mechanism in intercritically reheat-coarse grained heat-affected zone of X80 pipeline steel

Effect of Microstructure on Mechanical Properties of X65MS Welded Pipe Joint

Study on Local Brittle Zone Phenomena of Intercritically Reheated Coarse-Grained Heat-Affected Zone in Pipeline Steels

Microstructure and mechanical properties of X90 high strength pipeline steel

Experimental study on fracture toughness of high-strength structural steel and its butt weld

Microstructure Evolution and Alloying Features of A Developed High Strength and High Toughness Weld Metal Used for Pipeline Steels