Abstract:<p>A circumferential crack in the fusion line is a major threat to the structural integrity of the pipeline girth weld because it may possibly lead to fracture failure when subjected to large plastic deformations. For the newly constructed X80 pipeline with an outside diameter (OD) of 1422 mm in China, the complicated configuration of welded joints and the outer diameter are outside the range of the general fracture assessment standards, such as BS 7910. Furthermore, during the pipe manufacture process, pipeline designers merely specify the minimum yield strength limit according to the pipe steel grade. This results in a wide variation range in the choice of yield strength values of the base metal. This also leads to a serious problem in the fracture assessment of pipe girth weld because the weld strength is commonly considered to be either evenly matched or overmatched. The foregoing factors make it difficult to perform an accurate fracture assessment using conventional standards. This study therefore aims to investigate the fracture behavior of 1422-mm OD pipelines with a double-V groove weld and circumferential crack in the fusion line. The specific effect of material mismatch and the realistic operational parameters that influence the fracture capacity of the pipe are examined via a series of numerical investigations. First, a rigorous three-dimensional finite element model to simulate the pipe girth weld is established by utilizing the ABAQUS finite element code package. The weld, which has a canoe-shaped surface crack in the fusion line between the heat-affected zone and root welding metal, is subjected to biaxial loading conditions. The keyhole method is adopted to simulate the crack front as well as the crack tip to eliminate the stress singularity effect during deformation. A refined mesh strategy is introduced to ensure the accurate simulation of the stress and strain fields in the vicinity of the crack tip. Based on the numerical model, the J-integral fracture parameter, which is clearly defined based on a strict mechanical theory, is chosen to characterize the effect of strength matching ratio, internal pressure, and yield to tensile strength ratio on the crack driving force. A new strain-based J-integral prediction formula is proposed based on numerical results.</p>

Fracture Toughness Investigation of X100 Longitudinal Submerged Arc Welded Pipe Via Crack Tip Opening Displacement Test

Crack Tip Opening Displacement of X100 Sawl Pipe

FRACTURE TOUGHNESS OF WELDED JOINTS OF X100HIGH-STRENGTH PIPELINE STEEL

Experiment on the Fracture Toughness of Weld Joint of X70 Pipeline Steel

Experimental Research on Fracture Toughness of High Grade Line Pipe

Improving the Weld Heat-Affected-Zone (HAZ) Toughness of High-Strength Thick-Walled Line Pipes

FRACTURE TOUGHNESS OF X70 PIPELINE STEEL AT DIFFERENT TEMPERATURES

The Fracture Toughness of Butt Weld at Low Temperature of 960 MPa High-strength Steel

Experimental Study on Fracture Toughness of Butt Weld in Thick Plate Steel Structures at Low Temperature

Changes in microstructure and properties of weld heat-affected zone of high-strength low-alloy steel

Experimental study on fracture toughness of high-strength structural steel and its butt weld

Analysis on Cracking of a Pipeline Steel Pipe during Hydraulic Burst Test

Study on Fracture of Non-Through Crack Bodies of X60 Pipeline Steel

Impact of crack propagation path and inclusion elements on fracture toughness and micro-surface characteristics of welded pipes in DWTT

The fracture resistance and crack propagation path of L415/N08825 bimetallic composite pipe welded joint

Investigation on the weakest zone in toughness of 9Cr/NiCrMoV dissimilar welded joint and its enhancement

Role of microstructure heterogeneity on hydrogen-assisted fracture toughness degradation of X80 weld metal in H 2 S-saturated solution

Fracture response of 1422-mm diameter pipe with double-V groove weld joints and circumferential crack in fusion line

Study on Local Brittle Zone Phenomena of Intercritically Reheated Coarse-Grained Heat-Affected Zone in Pipeline Steels

Effect of H2S Corrosion on the Fracture Toughness of the X80 Pipeline Steel Welded Joint

Fracture driving forces of cracked girth welds with mechanical heterogeneity for X80 pipes