Abstract:Mechanical Performance of traditional gas-shielded arc welded joints of 700 MPa grade microalloyed C-Mn steel cannot meet service requirements. Laser welding, with its characteristic high energy density, is known to improve the welding performance of experimental steels. In the present study, Nb-Ti microalloyed steel with a thickness of 4.5 mm was welded using a 4 kW fiber laser. The microstructure, precipitation, and mechanical properties of the welded joints were studied. The hardness and tensile strength of the welded joints were higher than those of the base metal (BM). The microstructure of the fusion zone (FZ) and coarse grain heat affected zone (CGHAZ) was lath martensite (LM), while the microstructure of the fine grain HAZ and mixed grain HAZ consisted of ferrite and martensite/austenite islands. Although LM was observed in both the FZ and CGHAZ, the hardness and calculated tensile strength of the FZ were lower than those of the CGHAZ, due to a reduction in solid solution strengthening by element loss and the dissolution of high-hardness precipitates in FZ. Most precipitates such as [(Nb,Ti)C and (Nb,Ti)(C,N)] that were present in the BM were dissolved, which led to an increase in C and N in solid solution in the FZ. Thus, the elastic modulus of the FZ was higher than that of the BM. Similarly, the elastic modulus of the CGHAZ was higher than that of the BM due to the segregation of C and N atoms during the welding process. The toughness of the FZ was superior to that of the BM, and the toughness of the HAZ approached 91% of that of the BM. The change in toughness primarily depended on the microstructural refinement, the increase in the fraction of grains with high misorientation, the residual austenite in the FZ and CGHAZ, and the dissolution of coarse precipitates.

A comparative study of the microstructure and properties of 800 MPa microalloyed C-Mn steel welded joints by laser and gas metal arc welding

A comparative study on microstructure and mechanical properties of HG785D steel joint produced by hybrid laser-MAG welding and laser welding

Microstructure-Property Correlations in Fiber Laser Welded Nb-Ti Microalloyed C-Mn Steel

Microstructural evolution and mechanical properties of laser-welded joints of medium manganese steel

A Comparative Study on Microstructural Characterization of Thick High Strength Low Alloy Steel Weld by Arc Welding and Laser Welding

Microstructural Characteristics and Mechanical Properties in the Laser Beam Welded Joints of High-Strength Microalloyed Steel

Mirostructure and Properties of Laser Welded Joints of Dual Phase and Press-Hardened Steels

Effect of Welding Processes on Microstructure and Mechanical Properties of Laser-Welded Al-Si-Coated 22mnb5 Steel

Effect of Gas Metal Arc and Cold Metal Transfer Arc Welding Processes on Microstructure and Mechanical Properties of AA8011-H18 Alloy Joints

Comparison of Microstructure and Mechanical Properties of TIG and Laser Welding Joints of a New Al–Zn–Mg–Cu Alloy

Comparison of Microstructure and Mechanical Properties of Ultra-Narrow Gap Metal Active Gas Arc Welded and Narrow Gap Submerged Arc Welded Q235A Low Carbon Steel

Microstructure and Mechanical Properties of Welded Joints of Cr18Ni30Mo2Al3Nb Alloy

Study on microstructure and mechanical properties of Al-Mg-Mn-Er alloy joints welded by TIG and laser beam

Microstructure and mechanical properties of laser beam welding 6061 aluminum alloy with different states

Comparative study on microstructure and mechanical properties of laser welded–brazed Mg/mild steel and Mg/stainless steel joints

Comparison of Microstructure, Mechanical Properties, and Corrosion Behavior of Gas Metal Arc (GMA) and Ultrasonic-wave-assisted GMA (U-GMA) Welded Joints of Al–Zn–Mg Alloy

Microstructural, Porosity and Mechanical Properties of Lap Joint Laser Welding for 5182 and 6061 Dissimilar Aluminum Alloys under Different Place Configurations

The Microstructure and Mechanical Properties of Novel Cryogenic Twinning-Induced Plasticity Steel Welded Joint

Modifying Microstructures and Mechanical Properties of Laser-Arc Welded Joints of Dissimilar Advanced Aluminum Alloys

Comparison of Tensile Damage Evolution in Ti6A14V Joints Between Laser Beam Welding and Gas Tungsten Arc Welding

Microstructure and Properties in Dissimilar/similar Weld Joints Between DP780 and DP980 Steels Processed by Fiber Laser Welding