Abstract:The effect of aging temperature on precipitates in AZ80 magnesium alloy was studied by using environmental scanning electron microscope (ESEM) and transmission electron microscope (TEM). The precipitate/matrix orientation relationships (ORs) were measured, the precipitation mechanism was analyzed and the effect of precipitates on properties of alloy was tested. A new precipitated way of granular beta-Mg17Al12 phase was found in aged alloy, which was granular and nucleated at grain boundaries (GBs) and twin boundaries. Plate-like or graunlar-like beta-Mg17Al12 precipitated continuously in the alloy aged at higher temperature (310 degrees C). The plates were parallel to the basal plane of matrix, nucleated and grew homogeneously in grains, and had little effect on properties of alloy. Whereas the granular beta-phase was harmful for the alloy property. The discontinuous precipitation of beta-phase occurred at lower aged temperature (<250 degrees C), which was lamellar structure parallel or perpendicular to the basal plane of matrix, nucleated at grain boundaries and grew into grains. The grain boundaries moved into the grains with the growth of these discontinuous precipitates. The alloy was strengthened by the discontinuous precipitates evidently.

Influence of Aging Treatments on the Microstructure Evolution in Mg-8.8Hg-8Ga (wt%) Alloys

Influence of Aging Treatments on Microstructure and Electrochemical Properties in Mg–8.8Hg–8Ga (wt%) Alloy

Effects of solid solution and aging process on microstructure and mechanical properties of Mg-Gd-Y alloy

Influence of Aging Time on Mg-8al-1zn-3ca Alloy

Influence of Heat Treatment on Microstructure and Electrochemical Properties of Mg-5Hg-1Ga Alloy

Influence of Mg Contents on Aging Precipitation Behavior of Al–3.5Cu–xMg Alloy

Influence of Aging Time on Microstructure and Mechanical Properties of Mg-8Al-1Zn-3Ca Alloy

Microstructure evolution and performance of Mg-8Gd-3Y-1Nd-0.5Zr alloy during heat treatment

Effect of Aging Temperature on Microstructure and Mechanical Properties of Mg-12Gd-3Y-1Sm-0.5Zr Alloy

Precipitation and Its Effect on Age-Hardening Behavior of As-Cast Mg–Gd–Y Alloy

Influence of Mg5Ga2 Compound on Microstructures and Electrochemical Properties of Mg-5%Hg-22%Ga Alloy

Research on Solution and Aging Treatment of Mg-7Zn-3Al Alloy

Effect of Aging on Microstructure and Mechanical Properties of Mg-6Gd-3Y-0.4Zr-1Zn Alloy

Influences of Secondary Phase Mg3Hg Compound on the Electrochemical Properties of the Mg-5%Hg-1%Ga Alloys

Effect of aging on microstructure and hardness of Mg-5Y-3Sm-0.8Ca alloy

EFFECT OF HEAT TREATMENT ON MICROSTRUCTURE AND PROPERTIES OF AZ80 MAGNESIUM ALLOY

Microstructure, mechanical properties and fracture behavior of peak-aged Mg34Y32Nd31Gd alloys under different aging conditions

Determination of the Parameters of Precipitates in Aged Mg – 8% Zn – 4% Al – 0.2% Cr – 0.5% Bi Alloy

Effect of Aging Treatment on Tensile Behaviors of Cast Mg-9Gd-4Y-0.5Zr Alloy

Effects of Ag, Mg Micro-Alloying on Aging Characteristics and Microstructure of Al-Cu-Li Alloy

Effect of aging temperature on the hardening behavior and precipitation evolution of Mg 10Gd alloy