Abstract:The friction and wear behavior of WC based cemented carbides ring-ring samples in different water environments were systematically tested. The average grain size of WC is 1.2 μm and the mass fraction of binder Co is 8%. The water environments include distilled fresh water, artificial seawater with NaCl mass content of 4%, and sediment water with SiO 2 mass content of 0.6% and average particle size of 88 μm. The friction torque was measured for each friction pairs at different speeds and specific pressure loads. The surface morphology of the friction pairs before and after the test were observed by a scanning electron microscope, and the weight losses were also measured by a balance. The test results suggest that the friction coefficient of all the sample pairs decreases exponentially with the increase of load at proper revolution speed. In the range of 4–10 MPa specific pressure, the friction coefficient of the bearing during stable operation is between 0.01–0.02. The wear rate of the stationary ring is about 3 times that of the matching rotary ring, no matter in the environment of artificial seawater, distilled fresh water or sediment water lubrication medium. However, the wear rates of the samples in artificial seawater are higher than those of the two rings friction under the same speed and load conditions in the other two water environments. SiO 2 particles in the sediment water has no effect on the bearings wear rate. The wear of cemented carbide self-matching pair bearings is mainly the peeling of WC particles caused by the alternating contact and friction force or plowing of WC abrasive particles. The corrosivity of artificial seawater can aggravate the peeling of WC particles. The results and conclusions of this study can provide a meaningful reference for the design of cemented carbide bearings utilized in water lubrication environment.

Wear Behaviors of Cemented Carbide Cermet Yg8b under Different Concentrations of Abrasive Slurries from Carborundum, Corundum and Silica Sands

Wear Behaviors of Ticn Cermet under Different Concentrations of Abrasive Slurries from Carborundum, Corundum and Silica Sands

Dependence of Wear Behaviors of Hardmetal Yg8b on Coarse Abrasive Types and Their Slurry Concentrations

Abrasive Wear Behavior of Ticn Cermets under Water-Based Slurries with Different Abrasives

Wear Behaviour and Microstructural Changes of SiCw-Al Composite under Unlubricated Sliding Friction

Three-body abrasion behavior of ultrafine WC–Co hardmetal RX8UF with carborundum, corundum and silica sands in water-based slurries

Research On Wear Behavior Of Atc Cermet Material

Abrasive wear behavior of Sialon ceramic

Abrasive and adhesive wear behaviour of metallic bonds in a synthetic slurry test for wear prediction in reinforced concrete

Study on the Friction-Reducing Mechanisms of Surface Texture Cemented Carbide under Dry Sliding

Carburization And Wear Behavior Of Self-Lubricating Ti(C,N)-Based Cermets With Various Secondary Carbides

WEAR RESISTANCE OF CERAMIC MICROBEADS

Friction and dry sliding wear behaviour of cermets

Erosive Wear Performance and Mechanism of Engineering Ceramic Materials

Slurry Erosive Wear Characteristics of Engineering Ceramics for Hydraulic Machinery

Tribological characteristics of WC-Cr3C2-Ni cermet coatings under different wear parameters

Study of the Friction Behavior of Embedded Fibers in YG8 Surface Grooves

Frictional performance of silicon carbide under different lubrication conditions

Effect of Silica Size on the Relative Wear of Microstructures Containing Solidification Carbides and Tempered Martensite Using a Dry Sand Rubber Wheel Test

Erosion wear characteristics of cemented carbide for mud pulser rotor

Friction and wear behavior of cemented carbide self-matching pairs under different water lubrication conditions