Abstract:The moisture transport of axial-compression-damaged mortar and concrete was experimentally and analytically studied in this paper. Five stress levels, i.e., 25%, 40%, 55%, 70%, and 85%, of the corresponding ultimate compressive strengths were selected for mortar and concrete specimens with the water cement ratio (w/c) of 0.5. Porosities and sorptivities of mortar or concrete before and after axial compression were measured and compared. Based on the Lucas–Washburn equation on absorption, the relationship between sorptivity and pore size distribution as well as porosity was established. A damage-representative radius was proposed to simply quantify the variation of pore characteristics of damaged mortar and concrete, and the moisture transport of axial-compression-damaged mortar and concrete could be predicted by summing the contributions to water absorption from the original pore system and the pore-equivalent microcrack system. It is shown that the porosities of mortar and concrete only slightly increase with the damage level, but the sorptivities are sensitive to axial compression damage, i.e., increasing nearly monotonically with the stress level from 0.3326 to 0.3533 mm/min0.5 for damaged mortar specimens (w/c = 0.5) and from 0.1970 to 0.2226 mm/min0.5 for damaged concrete specimens (w/c = 0.5). The increase trend became more apparent for both materials after a threshold of 40–55% of the corresponding ultimate compressive strengths, which is within the service load of structures, indicating that damage should be considered for chloride ions and water transport in concrete in the tidal zone. The predicted moisture diffusivities of damaged mortar and concrete show marginal difference from those of sound materials because the damage-representative radius could be underestimated due to elastic recovery of materials after unloading.

Transport Properties of Concrete Altered by Crack-Induced Damage

Characterizing the effect of compressive damage on transport properties of cracked concretes

IMPACT OF CRACKING DAMAGE ON CONCRETE TRANSPORT PROPERTIES

Geometry of crack network and its impact on transport properties of concrete

Crack-altered durability properties and performance of structural concretes

Experimental Investigation on Transport Properties of Cement-Based Materials Incorporating 2D Crack Networks

Corrosion-Induced Cracking Propagation Of Rc Beams Subjected To Different Corrosion Methods And Load Levels

Characteristics of Concrete Cracks and Their Influence on Chloride Penetration

Moisture Transport of Axial-Compression-Damaged Mortar and Concrete in Atmospheric Environment

Model of Chloride Penetration into Cracked Concrete Subject to Drying–wetting Cycles

Quantification of Compression Induced Damage and Its Effect on the Chloride Transport in Structural Concrete

InfIuence of Ioad crack on chIoride diffusion in concrete

Effect of confining pressure and microcracks on mass transport properties of concrete

Comparative Analysis of Microdamage-affected Chloride Transport in Concrete under Static and Dynamic Hydraulic Pressure

Cracking Behavior of Cfrp Laminate-Strengthened Rc Beams with Premechanical and Postmechanical Environmental Damage

Water Transport in Unsaturated Cracked Concrete under Pressure

Theoretical and Experimental Investigation of Loading Effects on Chloride Diffusion in Saturated Concrete

A Numerical Study on Chloride Migration in Cracked Concrete Using Multi-Component Ionic Transport Models

Chloride transport in cracked concrete under wet-dry cycling condition

Moisture transports in high-cycle compressive fatigue-damaged concrete

INFLUENCE OF CRACKING WIDTH TO CONCRETE DURABILITY