Abstract:The moisture transport of axial-compression-damaged mortar and concrete was experimentally and analytically studied in this paper. Five stress levels, i.e., 25%, 40%, 55%, 70%, and 85%, of the corresponding ultimate compressive strengths were selected for mortar and concrete specimens with the water cement ratio (w/c) of 0.5. Porosities and sorptivities of mortar or concrete before and after axial compression were measured and compared. Based on the Lucas–Washburn equation on absorption, the relationship between sorptivity and pore size distribution as well as porosity was established. A damage-representative radius was proposed to simply quantify the variation of pore characteristics of damaged mortar and concrete, and the moisture transport of axial-compression-damaged mortar and concrete could be predicted by summing the contributions to water absorption from the original pore system and the pore-equivalent microcrack system. It is shown that the porosities of mortar and concrete only slightly increase with the damage level, but the sorptivities are sensitive to axial compression damage, i.e., increasing nearly monotonically with the stress level from 0.3326 to 0.3533 mm/min0.5 for damaged mortar specimens (w/c = 0.5) and from 0.1970 to 0.2226 mm/min0.5 for damaged concrete specimens (w/c = 0.5). The increase trend became more apparent for both materials after a threshold of 40–55% of the corresponding ultimate compressive strengths, which is within the service load of structures, indicating that damage should be considered for chloride ions and water transport in concrete in the tidal zone. The predicted moisture diffusivities of damaged mortar and concrete show marginal difference from those of sound materials because the damage-representative radius could be underestimated due to elastic recovery of materials after unloading.

Moisture transports in high-cycle compressive fatigue-damaged concrete

Development of Internal Moisture Transfer and Cumulative Residual Strain in Concrete under Freeze-Thaw Cycles

Predicting Fatigue Damage Growth in Cement-Treated Base Layer Built with Construction and Demolition Waste

Modeling Moisture Transport at the Surface Layer of Fatigue-Damaged Concrete

Chloride Penetration into Concrete Damaged by Uniaxial Tensile Fatigue Loading

Numerical Method for Creep Analysis of Strengthened Fatigue-Damaged Concrete Beams

Moisture Transport of Axial-Compression-Damaged Mortar and Concrete in Atmospheric Environment

Damage Based Constitutive Model for Predicting the Performance Degradation of Concrete

Comparative Analysis of Microdamage-affected Chloride Transport in Concrete under Static and Dynamic Hydraulic Pressure

Cracking Behavior of Cfrp Laminate-Strengthened Rc Beams with Premechanical and Postmechanical Environmental Damage

Influence of Flexural Loading on Chloride Ingress in Concrete Subjected to Cyclic Drying-Wetting Condition

Damage Degradation of Concrete Due to Compressive Fatigue Loading

Mesoscale Simulation of Fatigue Behavior of Concrete Materials Damaged by Freeze-Thaw Cycles

Theoretical and Experimental Investigation of Loading Effects on Chloride Diffusion in Saturated Concrete

Creep Characterization of Concrete Suffering Initial Damage

Model of Chloride Penetration into Cracked Concrete Subject to Drying–wetting Cycles

Characterizing the effect of compressive damage on transport properties of cracked concretes

Experimental investigations and micromechanical thermal fatigue models of concrete

Experimental Study on the Fatigue Damage of High Strength Concrete under Uniaxial Compression

Multiscale Analysis of Concrete Damage and Crack Propagation Under High Cycle Loading

Damage constitutive of concrete under uniaxial alternate tension?compression fatigue loading based on double bounding surfaces