Abstract:The A15 phase superconductor Nb3Al has been considered as an alternative to Nb3Sn for high field and large scale applications. However, to prepare a stoichiometric Nb3Al with fine grain structures is very difficult. High-energy ball milling is a solid state powder processing technique and is a very useful for preparing Nb-Al alloys (Nb3Al). The effects of ball milling time and annealing temperature on the formation of Nb3Al superconducting phase have been studied. Pure Nb and Al powders with stoichiometric ratio of Nb3Al were mixed and milled, and the charging and milling were performed in an inert atmosphere. Phase formation and structural evolution during high-energy ball milling have been examined by X-ray diffraction. Al disappeared and Nb peaks broadened after about one hour of milling. With increasing milling time, the peaks of Nb became considerably broader and intensities decreased, the Nb-Al solid solution phase was extensive when milled about 3 hours. In order to obtain Nb3Al superconducting phase, a subsequent anneal was required. We have annealed the as-milled powders at 800-900°C for different times to prepared Nb3Al superconducting alloy. The results indicated that Nb3Al with small amount of impurity phase can be obtained on annealing the Nb-Al solid solution phase and the superconducting transition temperature was about 15K, but it is difficult to obtain a homogeneous Nb3Al phase by annealing the amorphous powder.

Preparation of Nb3Al Powder by Chemical Reaction in Molten Salts

Direct synthesis of Nb–Al intermetallic nanoparticles by sodiothermic homogeneous reduction in molten salts

Preparation of Nb 3 Al Superconductor by Powder Metallurgy and Effect of Mechanical Alloying on the Phase Formation

Production Of Nbal3 Powders Through Sodium Reduction Of Oxides In Molten Salts

Production of NbAl 3 Powders Through Sodium Reduction of Oxides in Molten Salts

Preparation of Nb3al by High-Energy Ball Milling and Superconductivity

Study of Nb3Al Intermetallics Prepared by Laser Deposition

The Reaction Process of NbAl Interface in Rod-in-Tube Strands

Ternary-layered Cr2AlB2 synthesized from Cr, Al, and B powders by a molten salt-assisted method

Synthesis of Nano Sized Cr2AlC Powders by Molten Salt Method

Synthesis of Nb3Al high temperature intermetallic compound by laser deposition

Molten salt synthesis of orthorhombic CrB and Cr2AlB2 ceramics

A New Method for Preparing Titanium Aluminium Alloy Powder

Effect of Nb and Nb2O5 additives on mechano-thermal processing of TiAl/Al2O3 nano-composite

Novel Way to Synthesize Nanocrystalline Aluminum Nitride from Coarse Aluminum Powder

Electrochemical Synthesis of Nb-Doped BaTiO3 Nanoparticles with Titanium-Niobium Alloy as Electrode

Synthesizing AlN powder by mechanochemical reaction between aluminum and melamine

Preparation and Characterization of TiB2/Al3Ti/Al2O3 Composite Nano-powder

Synthesis of Nanosized NbN Powder with Cubic Structure by Ammonolysis Method

Control of Al Content During Ism Process of Nb3al

Synthesis of NiAl(Cr,Nb) Powder by Mechanical Alloying