Abstract:Highly ordered TiO2 nanotube array electrodes were successfully fabricated by a two-step anodization method on Ti sheet substrates in an electrolyte composed of ammonium fluoride, deionized water, and glycol. The tube wall was smooth, and the average internal and external diameters, wall thickness, and tube length achieved were 80 nm, 90 nm, 10 nm, and 9 μm, respectively. X-ray diffraction and field emission scanning electron microscopy results revealed that the TiO2 nanotube arrays presented an amorphous structure. When calcined at 300 °C, the arrays crystallized into the anatase phase, and the crystallization degree of the oxide layer increased as the temperature rose. Calcinating at 400 °C did not obviously disrupt the porous structure of the highly ordered arrays. However, higher temperature enlarged the diameter of the nanotube array and roughened the tube wall. When the temperature reached 600 °C, the nanotube mouth broke because of the excessive stress, causing the oxide layer’s thinness and nanotube mouth clogging. The photoelectric test showed that the electrode presented obvious photoresponse under 300–400 nm UV excitation (maximized at 360 nm). The degree of crystallization and the micro-structure of the oxide layer can significantly affect the photoelectric properties of the electrode. After calcination at 400 °C, the TiO2 nanotube arrays, with highly ordered tubular structure directly connected to the Ti substrate, can ensure the rapid transportation of photo-induced electrons to the Ti substrate, while the high crystallinity of the arrays can help reduce the defect density of the nanotube and extend the lifetime of the photo-induced carriers. The electrode showed the best photoelectric property, and the photocurrent intensity was maximized (29.6 μA). However, the calcination process with over-temperature resulted in substantial loss of the TiO2 oxide layer, mouth clogging, and a severe decline in the photoelectric properties.

Fabrication and photodegradation properties of TiO 2 nanotubes on porous Ti by anodization

Preparation and Photocatalytic Activities of TiO2 Nanotubes with Mixed Crystal Structure

Temperature-dependent differences in wettability and photocatalysis of TiO 2 nanotube arrays thin films

Comparative Analysis of Anodized TiO2 Nanotubes and Hydrothermally Synthesized TiO2 Nanotubes: Morphological, Structural, and Photoelectrochemical Properties

Fabrication of TiO2 Nanotube by Electrochemical Anodization: Toward Photocatalytic Application

Fabrication and Photocatalytic Activity of Tio2 Nanofiber Membrane

TiO2 Nanotubes with Tunable Morphology, Diameter, and Length: Synthesis and Photo-Electrical/Catalytic Performance

Fabrication of Porous Tio2 Film Via Hydrothermal Method and Its Photocatalytic Performances

Preparation of TiO2 Nanotube Photocatalyst by Anodization and Improvement of Photocatalytic Performance

Fabrication and Photocatalysis of TiO2 Flower-like Nanostructures

Study on Fabrication and UV Photoelectric Property of TiO2 Nanotube Array Electrodes.

Anodization Fabrication of Highly Ordered Tio2 Nanotubes

Hydrothermal Preparation of TiO2 Nanotubes and Its Photocatalytic Performance

Fabrication of Titanium Oxide Nanotube Arrays by Anodic Oxidation

Fabrication of multi-non-metal-doped TiO2 nanotubes by anodization in mixed acid electrolyte

Effect of annealing temperature on morphology, structure and photocatalytic behavior of nanotubed H2Ti2O4(OH)2

Crystal phase transition and properties of titanium oxide nanotube arrays prepared by anodization

Hydrothermal Preparation of Nanoporous Tio2 Films with Exposed {001} Facets and Superior Photocatalytic Activity

Fabrication of Double-Walled TiO2 Nanotubes with Bamboo Morphology Via One-Step Alternating Voltage Anodization

Enhanced Hydrogen Production on Porous Tio2 Nanotube Arrays

Preparation of TiO2 Nanotubes and Its Degradation Properties of Nonylphenol