Abstract:Using the Raney Fe-Al alloy as the precursor for Fe and Al, and tetrapropylammonium hydroxide (TPAOH) as both the base for the leaching of the alloy and the template for the synthesis of HZSM-5, we synthesized the skeletal Fe core-HZSM-5 shell catalysts (Raney Fe@HZSM-5) via a facile one-pot hydrothermal strategy. The thickness of the zeolite shell was adjusted by varying the hydrothermal time. The catalysts were characterized by inductively coupled plasma-atomic emission spectroscopy (ICP-AES), N-2 physisorption, X-ray powder diffraction (XRD), temperature-programmed desorption of NH3 (NH3-TPD), and scanning electron microscopy (SEM). It was identified that the Raney Fe-Al alloy was more suitable than the rapidly quenched Fe-Al alloy as the precursor to the skeletal Fe core, since the skeletal Fe catalyst alkali-leached from the former produced more long-chain hydrocarbons during the Fischer-Tropsch synthesis (FTS) reaction for successive cracking and isomerization. A complete HZSM-5 shell was obtained only after above 24 h of hydrothermal treatment. With the hydrothermal time from 2 d to 8 d, the thickness of the compact HZSM-5 shell increased from 1.3 mu m to 9.7 mu m, the relative crystallinity increased steadily, while the SiO2/Al2O3 ratio remained essentially constant, and the amount of the acid sites is parallel to the thickness of the zeolite shell. In the FTS reaction using syngas with the H-2/CO molar ratio of 2 and at 543 and 2.0 MPa, the CO conversion and the selectivity to the gasoline fraction (C-5 similar to C-11 hydrocarbons) evolved in a volcanic trend with the shell thickness, suggesting the existence of an optimal amount of the acid sites, while less or more is adverse to the activity and selectivity to the gasoline fraction. The Raney Fe@HZSM-5 catalyst hydrothermally treated for 4 d exhibited the highest CO conversion of 92% and the selectivity to the gasoline fraction of 71%, along with an iso-paraffin to n-paraffin ratio of 1.9. At the n(H-2)/n(CO) ratio of 1, the selectivity to the gasoline fraction and the iso-paraffin to n-paraffin ratio were further improved to 73% and 2.1, respectively, which shows promise for this catalyst to transform the coal- or biomass-derived syngas to high-octane number gasoline.

Synthesis of Monolithic Al-fiber@HZSM-5 Core-Shell Catalysts for Methanol-to-propylene Reaction

A facile route to synthesize endurable mesopore containing ZSM-5 catalyst for methanol to propylene reaction.

Methanol to Propylene over Foam SiC-Supported ZSM-5 Catalyst: Performance of Multiple Reaction–Regeneration Cycles

Phosphorous Modified High Silica ZSM-5 Spherical Catalyst and Its Reaction on Methanol to Propylene

Optimization of Conditions for Preparation of ZSM-5@silicalite-1 Core–shell Catalysts Via Hydrothermal Synthesis

Catalytic Study of Methanol-to-Propylene Conversion over Nano-Sized HZSM-5

Programmable synthesis of mesoporous ZSM-5 nanocrystals as selective and stable catalysts for the methanol-to-propylene process

Effect of the Si/Al Ratios of Nanocrystalline HZSM-5 Zeolite on the Performance in Catalytic Conversion of Ethanol to Propylene

Regulation of framework Al distribution of high-silica hierarchically structured ZSM-5 zeolites by boron-modification and its effect on materials catalytic performance in methanol-to-propylene reaction

Influence of framework Al distribution in HZSM-5 channels on catalytic performance in the methanol to propylene reaction

Conversion of Methanol to Propylene over a High Silica B-HZSM-5 Catalyst

High Throughput Research and Development of Catalysts for Converting Methanol into Propylene

Selective production of propylene from methanol: Mesoporosity development in high silica HZSM-5

Direct synthesis of HZSM-5 zeolites with enhanced catalytic performance in the methanol-to-propylene reaction

Control of the proximity of bifunctional zeolite@Al2O3 catalysts for efficient methanol conversion into hydrocarbons

Synthesis of ZSM-5 Catalysts with Tunable Mesoporosity by Ultrasound-Assisted Method: A Highly Stable Catalyst for Methanol to Propylene

Conversion of methanol to propylene over hierarchical HZSM-5: the effect of Al spatial distribution.

Effect of Shell Thickness on Skeletal Fe@HZSM-5 Core-Shell Catalysts for Fischer-Tropsch Synthesis

Controllable Fabrication of Uniform Core–shell Structured Zeolite@sba-15 Composites

The synthesis of endurable B–Al–ZSM-5 catalysts with tunable acidity for methanol to propylene reaction

High-performance HZSM-5/cordierite Monolithic Catalyst for Methanol to Propylene Reaction: A Combined Experimental and Modelling Study