Abstract:In the present work, mesoporosity is introduced into highly siliceous HZSM-5 zeolites (SiO2/Al2O3 = 400) by a two-step path including desilication using NaAlO2 and TPAOH (tetrapropylammonium hydroxide) mixtures, followed by acid washing treatment. The physicochemical properties of conventional microporous HZSM-5 and all treated samples were characterized by ICP-OES, XRD, FE-SEM, BET and NH3-TPD methods. The catalytic performance of the HZSM-5 samples was determined in methanol to propylene conversion reaction at 460 °C and methanol WHSV of 0.9 h-1 using feed containing 50 wt% methanol in water. The results showed that the porosity of the desilicated samples has been mainly blocked by sodium aluminate derived deposits and silicon-containing debris. After a subsequent acid washing step with hydrochloric acid, the blocking species were removed which resulted in improving the mesoporosity generated in the desilication step. It was found that alkaline-acid treatment in a NaAlO2/TPAOH solution with TPAOH/(NaAlO2 + TPAOH) = 0.4 followed by acid washing, leads to the formation of narrow and uniform mesoporosity without severely destroying the crystal structure. Also, it exhibits higher selectivities to propylene (37.7 vs. 30.7%) and total butylenes (21.2 vs. 16.1%), propylene to ethylene ratio (4.0 vs. 2.7), as well as total light olefins (68.4 vs. 57.9%) compared to the parent catalyst, while its selectivities to C1-C4 alkanes (9.6 vs. 13.7%) and heavy hydrocarbons (13.8 vs. 28.4%) are relatively lower. The lifetime of the optimum alkaline-acid treated sample (640 h) showed a significant increase compared to that of the parent catalyst (425 h). The results exhibited that desilication process leads to a considerable mesoporosity development, while acid washing treatment mostly influences on the catalyst acidity. Therefore, the combination of the alkaline-acid treatment leads to hierarchical HZSM-5 catalyst formation with tailored pore architecture and surface acidic properties.

Conversion of methanol to propylene over hierarchical HZSM-5: the effect of Al spatial distribution.

Research progress of hierarchical zeolites for methanol to propylene reaction

Phosphorous Modified High Silica ZSM-5 Spherical Catalyst and Its Reaction on Methanol to Propylene

Catalytic Study of Methanol-to-Propylene Conversion over Nano-Sized HZSM-5

Effect of the Si/Al Ratios of Nanocrystalline HZSM-5 Zeolite on the Performance in Catalytic Conversion of Ethanol to Propylene

Conversion of Methanol to Propylene over a High Silica B-HZSM-5 Catalyst

Selective production of propylene from methanol: Mesoporosity development in high silica HZSM-5

Regulation of framework Al distribution of high-silica hierarchically structured ZSM-5 zeolites by boron-modification and its effect on materials catalytic performance in methanol-to-propylene reaction

Direct synthesis of HZSM-5 zeolites with enhanced catalytic performance in the methanol-to-propylene reaction

Influence of framework Al distribution in HZSM-5 channels on catalytic performance in the methanol to propylene reaction

Preparation of hierarchical HZSM-5 zeolites with combined desilication with NaAlO2/tetrapropylammonium hydroxide and acid modification for converting methanol to propylene

Methanol to Propylene: Effect of Phosphorus on a High Silica HZSM-5 Catalyst

Preparation of hierarchical H-[B]-ZSM-5 zeolites by a desilication method as a highly selective catalyst for conversion of methanol to propylene

Synthesis of hierarchical ZSM-11 and its catalytic performances during methanol to propylene

The effect of hierarchical single-crystal ZSM-5 zeolites with different Si/Al ratios on its pore structure and catalytic performance

Enhancement of 1-Propanol Selectivity in Propene Hydration over Zeolites HNU-3 and HZSM-5

Facile synthesis of hierarchical H-[B]-ZSM-5 aggregates via design-optimized desilication for enhanced methanol-to-propylene conversion

Optimization of Conditions for Preparation of ZSM-5@silicalite-1 Core–shell Catalysts Via Hydrothermal Synthesis

Effect of Si/Al2 Ratio on Catalytic Performance of HZSM-5 Zeolites for Conversion of Ethanol to Propylene

Synthesis of a Hierarchical ZSM-11/5 Composite Zeolite of High SiO 2 /al 2 O 3 Ratio and Catalytic Performance in the Methanol-to-olefins Reaction

Highly stable boron-modified hierarchical nanocrystalline ZSM-5 zeolite for the methanol to propylene reaction