Abstract:The core–shell with regular morphology was prepared through an innovative tandem synthesis strategy for the first time, which combined the insertion of almost all aluminum sites by organotemplate-free synthesis and the sequential crystallization of residual silica sites by organotemplate-oriented synthesis. Samples with different Si and Al distributions could be synthesized by adjusting the tandem synthesis process, including temperature, time, Na2O/SiO2, etc. The obtained Si-rich-ZSM-5 and conventional C-ZSM-5 with a similar Si/Al ratio but different Al distributions, which were demonstrated by X-ray fluorescence (XRF), X-ray photoelectron spectroscopy (XPS), Transmission electron microscopy (TEM), and 1,3,5-triisopropylbenzene catalytic cracking analysis, were employed in n-hexane catalytic cracking reaction. Si-rich-ZSM-5 showed a higher stability with a n-hexane conversion of 57.7% at 100 h compared with that of C-ZSM-5 (24.6%), which was attributed to its inactive outer shell. Besides, a high para-xylene selectivity in xylene for the Si-rich-ZSM-5 catalyst was obtained. Hence, this study provides a simple and cost-effective strategy to fabricate highly stable catalysts for cracking reactions.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.iecr.1c01043?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.iecr.1c01043</a>.Discussions of materials and synthetic methods used, tables of synthesis conditions, physicochemical properties, and number of acid sites of different ZSM-5 samples, and figures of SEM and TEM images, XRD patterns, N2 adsorption–desorption isotherms, Al concentration, TEM-EDS analyses, optical photographs of the used catalysts, thermogravimetric curves, selectivity with TOS, n-hexane uptake kinetics curves, and product distributions with time on stream (<a class="ext-link" href="/doi/suppl/10.1021/acs.iecr.1c01043/suppl_file/ie1c01043_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Optimization of Conditions for Preparation of ZSM-5@silicalite-1 Core–shell Catalysts Via Hydrothermal Synthesis

Effect of Hydrothermal Treatment on Suppressing Coking of Zsm-5 Zeolite During Methanol-To-Propylene Reaction

Core–Shell HZSM-5@silicalite-1 Composite: Controllable Synthesis and Catalytic Performance in Alkylation of Toluene with Methanol

Synthesis and Physicochemical Characterization of Hierarchical ZSM-5: Effect of Organosilanes on the Catalyst Properties and Performance in the Catalytic Fast Pyrolysis of Biomass

Effects of Silicalite-1 Coating on the p-Xylene Selectivity and Catalytic Stability of HZSM-5 in Toluene Methylation with Methanol

Promising Strategy to Synthesize ZSM-5@Silicalite-1 with Superior Catalytic Performance for Catalytic Cracking Reactions

Synthesis of CuO–ZnO–Al2O3 @ SAPO-34 Core@shell Structured Catalyst by Intermediate Layer Method

An efficient synthesis protocol of core-shell ZSM-5@Silicalite-1 for the targeted alkylation reaction of toluene with ethanol

Sustainable Synthesis of Core-shell Structured ZSM-5@Silicalite-1 Zeolite

Si/Al Ratio Induced Structure Evolution During Desilication-Recrystallization of Silicalite-1 to Synthesize Nano-Zsm-5 Catalyst for MTH Reaction

Solvent-Free Synthesis of Core–Shell Zn/ZSM-5@Silicalite-1 Catalyst for Selective Conversion of Methanol to BTX Aromatics

ZSM-5@MCM-41 core–shell composite with tunable shell thickness for n -heptane catalytic cracking reaction

Surfactant-assisted hydrothermal synthesis of core-shell ZSM-5@SSZ-13 zeolite for methanol to olefins reaction

Synthesis of hollow HZSM-5 zeolite-based catalysts and catalytic performance in MTA reaction

Synthesis of ZSM-5 Catalysts with Tunable Mesoporosity by Ultrasound-Assisted Method: A Highly Stable Catalyst for Methanol to Propylene

Silicalite-1 Derivational Desilication-Recrystallization to Prepare Hollow Nano-ZSM-5 and Highly Mesoporous Micro-ZSM-5 Catalyst for Methanol to Hydrocarbons

Controllable Synthesis of Nano-Zsm-5 Catalysts with Large Amount and High Strength of Acid Sites for Conversion of Methanol to Hydrocarbons

Coating mesoporous ZSM-5 by microporous silicalite-1 shell: Preparation and enhanced catalytic properties in methane co-aromatization with propane

Direct synthesis of HZSM-5 zeolites with enhanced catalytic performance in the methanol-to-propylene reaction

Regulating Hierarchical Structure and Acidity of HZSM-5 for Methanol to Aromatics Via Protective Desiliconization and External Surface Modification

Effect of Preparation Method on the Catalytic Performance of HZSM-5 Zeolite Catalysts in the MTH Reaction