Abstract:Large crystalline particles of ZSM-5 zeolites (S-ZSM-S) have been successfully synthesized by adjusting crystallization time and Si/A1 ratios in the starting solid mixtures in the absence of water solvent. Catalytic tests in the methanol-to-olefins (MTO) reaction show that these S-ZSM-5 zeolites obtained from the solvent-free route exhibit superior catalytic properties including excellent propylene selectivity and extraordinarily long life in the MTO reaction. Particularly, when the crystallization time is 30 h and the Si/A1 ratio in the starting solid mixture is adjusted at 150 under the solvent-free conditions, the S-ZSM-5-30h-LS0 catalyst with the large particle sizes (10-20 mu m) gives propylene selectivity as high as 50.0% and catalyst life as long as 9 h, which are much better than those (propylene selectivity at 38.9% and catalyst life of 3 h) of the conventional ZSM-5 zeolite with smaller crystals (ca. 5 mu m) synthesized from the hydrothermal route. High-resolution TEM images of these S-ZSM-S zeolites demonstrate that there is mesoporosity in the samples. More interestingly, these mesopore size distributions could be adjusted by the crystallization time during the solvent-free synthesis. Obviously, the presence of mesoporosity is very favorable for the mass transfer, and an appropriate Si/A1 ratio in the zeolite framework could offer suitable acidic density for the catalytic conversion, which should be responsible for the superior catalytic properties in the MTO over the S-ZSM-5-30h-150 catalyst. The features of mesoporosity in the S-ZSM-5 crystals and sustainability for the solvent-free synthesis could be potentially important for wide applications of these S-ZSM-5 zeolites in the future.

Synthesis of ZSM-5 Catalysts with Tunable Mesoporosity by Ultrasound-Assisted Method: A Highly Stable Catalyst for Methanol to Propylene

A facile route to synthesize endurable mesopore containing ZSM-5 catalyst for methanol to propylene reaction.

Effect of Hydrothermal Treatment on Suppressing Coking of Zsm-5 Zeolite During Methanol-To-Propylene Reaction

Mesoporogen-Free Synthesis of High-Silica Hierarchically Structured ZSM-5 Zeolites and Their Superior Performance for the Methanol-to-Propylene Reaction

Solvent-free and Mesoporogen-free Synthesis of Mesoporous Aluminosilicate ZSM-5 Zeolites with Superior Catalytic Properties in the Methanol-to-Olefins Reaction

Programmable synthesis of mesoporous ZSM-5 nanocrystals as selective and stable catalysts for the methanol-to-propylene process

Fabrication of Hollow Mesoporous Nanosized ZSM‐5 Catalyst with Superior Methanol‐to‐Hydrocarbons Performance by Controllable Desilication

Direct synthesis of HZSM-5 zeolites with enhanced catalytic performance in the methanol-to-propylene reaction

Hierarchically Tetramodal-Porous Zeolite ZSM-5 Monoliths with Template-Free-derived Intracrystalline Mesopores

Controlling the Morphologies and Crystal Growth Orientations of H-ZSM-5: Their Impact on the Structure-Diffusion-performance Relationship in the Methanol-to-propylene Reaction

High-silica hierarchical ZSM-5 prepared by conventional alkali treatment: A highly stable MTP catalyst

Highly stable boron-modified hierarchical nanocrystalline ZSM-5 zeolite for the methanol to propylene reaction

The synthesis of endurable B–Al–ZSM-5 catalysts with tunable acidity for methanol to propylene reaction

Three-step short-time temperature-programmed hydrothermal synthesis of ZSM-5 with high durability for conversion of methanol to propylene

Fluoride-mediated Nano-Sized High-Silica ZSM-5 As an Ultrastable Catalyst for Methanol Conversion to Propylene

Facile synthesis of hierarchical macro/microporous ZSM-5 zeolite with high catalytic stability in methanol to olefins

F-assisted synthesis of a hierarchical ZSM-5 zeolite for methanol to propylene reaction: a b-oriented thinner dimensional morphology

Synthesis of hierarchical ZSM-11 and its catalytic performances during methanol to propylene

In-Situ Synthesis of Zsm-5 Zeolite from Metakaolin/Spinel and Its Catalytic Performance on Methanol Conversion

Synergistic Effect of Structure and Morphology of ZSM-5 Catalysts on the Transformation of Methanol to Propylene

Improved catalytic performance of mesoporous ZSM-5 nanocrystalline zeolite prepared by the cationic surfactant-ammonium salt mixed agent method in the methanol to gasoline reaction