Abstract:Nano-ZSM-5 with large amount and high strength of acid sites were successfully synthesized by hydrothermal crystallization of pure-silica nucleus in NaAlO2 alkali solution. The concentration of NaAlO2 alkali solution was decreased by increasing the H2O/Al ratio from 200 to 2600, which strongly determined the acidic properties and crystal size of the obtained nano-ZSM-5. Low concentration of NaAlO2 alkali solution was found unfavorable for the incorporation of Al into the bulk of ZSM-5 crystal in crystallization process. Hence, more Al distributed at the exterior of crystals, which enhanced the accessibility of the acid sites during reaction. Large amount and high strength of acid sites were produced for nano-ZSM-5 by increasing H2O/Al ratio. When the H2O/Al ratio increased from 200 to 2600, the total amount of acid sites increased from 0.59 to 0.81 mmol g(-1), much higher than conventional value of 0.50 mmol g(-1). In addition, the acid strength increased and the ratio of Bronsted/Lewis acid sites were sharply increased from 2.3 to 4.1 when the H2O/Al ratio increased. Moreover, the size of nano-crystal was also decreased by above decreasing the concentration of the NaAlO2 alkali solution. When the H2O/Al ratio was 2600, the obtained sample possessed total acid amount of 0.81 mmol g(-1) and crystal size of 60 nm, respectively. Methanol to hydrocarbon (MTH) reaction results showed that the increased acid sites of the catalyst decreased its catalytic lifetime to some extent, but the aromatics selectivity was tunable obviously. As for the catalyst prepared with H2O/Al ratio of 2000, the aromatics selectivity of the obtained catalyst reached to 66.0%. This paper provided a method for the fabrication of small-size nano-ZSM-5 with large amount and high strength of acid sites and regulated Al distribution for MTH reaction.

Three-step short-time temperature-programmed hydrothermal synthesis of ZSM-5 with high durability for conversion of methanol to propylene

Methanol to Propylene over Foam SiC-Supported ZSM-5 Catalyst: Performance of Multiple Reaction–Regeneration Cycles

Effect of Hydrothermal Treatment on Suppressing Coking of Zsm-5 Zeolite During Methanol-To-Propylene Reaction

Catalytic Properties and Reaction Behaviors of ZSM-5 Catalysts in Different MTP Reaction-Regeneration Cycles

ZSM-5 Crystals Grown on the Wall of a Long Tubular Reactor As a Structured Catalyst for Cracking of Endothermic Fuels

A facile route to synthesize endurable mesopore containing ZSM-5 catalyst for methanol to propylene reaction.

Synthesis of ZSM-5 Catalysts with Tunable Mesoporosity by Ultrasound-Assisted Method: A Highly Stable Catalyst for Methanol to Propylene

High-silica hierarchical ZSM-5 prepared by conventional alkali treatment: A highly stable MTP catalyst

Optimization of Conditions for Preparation of ZSM-5@silicalite-1 Core–shell Catalysts Via Hydrothermal Synthesis

Synthesis of hierarchical ZSM-11 and its catalytic performances during methanol to propylene

Direct synthesis of HZSM-5 zeolites with enhanced catalytic performance in the methanol-to-propylene reaction

High Throughput Research and Development of Catalysts for Converting Methanol into Propylene

Preparation of H-[B]- ZSM -5 zeolites by hydrothermal method as a highly stable and selective catalyst for methanol to propylene (MTP) conversion

Facile synthesis of hierarchical H-[B]-ZSM-5 aggregates via design-optimized desilication for enhanced methanol-to-propylene conversion

High-performance HZSM-5/cordierite Monolithic Catalyst for Methanol to Propylene Reaction: A Combined Experimental and Modelling Study

Advances in Catalytic Conversion of Methanol to Propylene

Effect of Preparation Method on the Catalytic Performance of HZSM-5 Zeolite Catalysts in the MTH Reaction

Controllable Synthesis of Nano-Zsm-5 Catalysts with Large Amount and High Strength of Acid Sites for Conversion of Methanol to Hydrocarbons

Synthesis of nano-size HZSM-5 and their performances in MTP reaction

Conversion of Methanol to Propylene over a High Silica B-HZSM-5 Catalyst

Nanocrystalline HZSM‐5prepared by Supercritical Hydrothermal Synthesis and Its Catalytic Esterification Performances