Abstract:In the present work, mesoporosity is introduced into highly siliceous HZSM-5 zeolites (SiO2/Al2O3 = 400) by a two-step path including desilication using NaAlO2 and TPAOH (tetrapropylammonium hydroxide) mixtures, followed by acid washing treatment. The physicochemical properties of conventional microporous HZSM-5 and all treated samples were characterized by ICP-OES, XRD, FE-SEM, BET and NH3-TPD methods. The catalytic performance of the HZSM-5 samples was determined in methanol to propylene conversion reaction at 460 °C and methanol WHSV of 0.9 h-1 using feed containing 50 wt% methanol in water. The results showed that the porosity of the desilicated samples has been mainly blocked by sodium aluminate derived deposits and silicon-containing debris. After a subsequent acid washing step with hydrochloric acid, the blocking species were removed which resulted in improving the mesoporosity generated in the desilication step. It was found that alkaline-acid treatment in a NaAlO2/TPAOH solution with TPAOH/(NaAlO2 + TPAOH) = 0.4 followed by acid washing, leads to the formation of narrow and uniform mesoporosity without severely destroying the crystal structure. Also, it exhibits higher selectivities to propylene (37.7 vs. 30.7%) and total butylenes (21.2 vs. 16.1%), propylene to ethylene ratio (4.0 vs. 2.7), as well as total light olefins (68.4 vs. 57.9%) compared to the parent catalyst, while its selectivities to C1-C4 alkanes (9.6 vs. 13.7%) and heavy hydrocarbons (13.8 vs. 28.4%) are relatively lower. The lifetime of the optimum alkaline-acid treated sample (640 h) showed a significant increase compared to that of the parent catalyst (425 h). The results exhibited that desilication process leads to a considerable mesoporosity development, while acid washing treatment mostly influences on the catalyst acidity. Therefore, the combination of the alkaline-acid treatment leads to hierarchical HZSM-5 catalyst formation with tailored pore architecture and surface acidic properties.

A facile route to synthesize endurable mesopore containing ZSM-5 catalyst for methanol to propylene reaction.

Methanol to Propylene over Foam SiC-Supported ZSM-5 Catalyst: Performance of Multiple Reaction–Regeneration Cycles

Preparation of Mesopore Containing Zeolite ZSM-5 and Its Application in Methanol to Propylene Reaction

Programmable synthesis of mesoporous ZSM-5 nanocrystals as selective and stable catalysts for the methanol-to-propylene process

Synthesis of ZSM-5 Catalysts with Tunable Mesoporosity by Ultrasound-Assisted Method: A Highly Stable Catalyst for Methanol to Propylene

Solvent-free and Mesoporogen-free Synthesis of Mesoporous Aluminosilicate ZSM-5 Zeolites with Superior Catalytic Properties in the Methanol-to-Olefins Reaction

Highly stable boron-modified hierarchical nanocrystalline ZSM-5 zeolite for the methanol to propylene reaction

The synthesis of endurable B–Al–ZSM-5 catalysts with tunable acidity for methanol to propylene reaction

Surfactant-assisted hydrothermal synthesis of core-shell ZSM-5@SSZ-13 zeolite for methanol to olefins reaction

Direct synthesis of HZSM-5 zeolites with enhanced catalytic performance in the methanol-to-propylene reaction

Facile synthesis of rodlike ZSM-5 zeolite microspheres and catalytic performance in methanol to propylene reaction

Controllable Fabrication of Uniform Core–shell Structured Zeolite@sba-15 Composites

High-silica hierarchical ZSM-5 prepared by conventional alkali treatment: A highly stable MTP catalyst

Facile synthesis of hierarchical macro/microporous ZSM-5 zeolite with high catalytic stability in methanol to olefins

In-situ synthesis of hierarchical lamellar ZSM-5 zeolite with enhanced MTP catalytic performance by a facile seed-assisted method

Solid-conversion synthesis of three-dimensionally ordered mesoporous ZSM-5 catalysts for the methanol-to-propylene reaction

Facile synthesis of hierarchical H-[B]-ZSM-5 aggregates via design-optimized desilication for enhanced methanol-to-propylene conversion

Hierarchically Tetramodal-Porous Zeolite ZSM-5 Monoliths with Template-Free-derived Intracrystalline Mesopores

Preparation of hierarchical HZSM-5 zeolites with combined desilication with NaAlO2/tetrapropylammonium hydroxide and acid modification for converting methanol to propylene

Sustainable Synthesis of Core-shell Structured ZSM-5@Silicalite-1 Zeolite

A simple route to synthesize mesoporous ZSM-5 templated by ammonium-modified chitosan.