Abstract:Nano-ZSM-5 with large amount and high strength of acid sites were successfully synthesized by hydrothermal crystallization of pure-silica nucleus in NaAlO2 alkali solution. The concentration of NaAlO2 alkali solution was decreased by increasing the H2O/Al ratio from 200 to 2600, which strongly determined the acidic properties and crystal size of the obtained nano-ZSM-5. Low concentration of NaAlO2 alkali solution was found unfavorable for the incorporation of Al into the bulk of ZSM-5 crystal in crystallization process. Hence, more Al distributed at the exterior of crystals, which enhanced the accessibility of the acid sites during reaction. Large amount and high strength of acid sites were produced for nano-ZSM-5 by increasing H2O/Al ratio. When the H2O/Al ratio increased from 200 to 2600, the total amount of acid sites increased from 0.59 to 0.81 mmol g(-1), much higher than conventional value of 0.50 mmol g(-1). In addition, the acid strength increased and the ratio of Bronsted/Lewis acid sites were sharply increased from 2.3 to 4.1 when the H2O/Al ratio increased. Moreover, the size of nano-crystal was also decreased by above decreasing the concentration of the NaAlO2 alkali solution. When the H2O/Al ratio was 2600, the obtained sample possessed total acid amount of 0.81 mmol g(-1) and crystal size of 60 nm, respectively. Methanol to hydrocarbon (MTH) reaction results showed that the increased acid sites of the catalyst decreased its catalytic lifetime to some extent, but the aromatics selectivity was tunable obviously. As for the catalyst prepared with H2O/Al ratio of 2000, the aromatics selectivity of the obtained catalyst reached to 66.0%. This paper provided a method for the fabrication of small-size nano-ZSM-5 with large amount and high strength of acid sites and regulated Al distribution for MTH reaction.

The synthesis of endurable B–Al–ZSM-5 catalysts with tunable acidity for methanol to propylene reaction

A facile route to synthesize endurable mesopore containing ZSM-5 catalyst for methanol to propylene reaction.

Methanol to Propylene over Foam SiC-Supported ZSM-5 Catalyst: Performance of Multiple Reaction–Regeneration Cycles

Phosphorous Modified High Silica ZSM-5 Spherical Catalyst and Its Reaction on Methanol to Propylene

Highly stable boron-modified hierarchical nanocrystalline ZSM-5 zeolite for the methanol to propylene reaction

Regulation of framework Al distribution of high-silica hierarchically structured ZSM-5 zeolites by boron-modification and its effect on materials catalytic performance in methanol-to-propylene reaction

Preparation of H-[B]- ZSM -5 zeolites by hydrothermal method as a highly stable and selective catalyst for methanol to propylene (MTP) conversion

Synthesis of ZSM-5 Catalysts with Tunable Mesoporosity by Ultrasound-Assisted Method: A Highly Stable Catalyst for Methanol to Propylene

Influence of Acid-Base Properties of ZnMgAl-mixed Oxides for the Synthesis of 1-Methoxy-2-propanol

High-silica hierarchical ZSM-5 prepared by conventional alkali treatment: A highly stable MTP catalyst

Direct synthesis of HZSM-5 zeolites with enhanced catalytic performance in the methanol-to-propylene reaction

Synthesis of hierarchical ZSM-11 and its catalytic performances during methanol to propylene

High Throughput Research and Development of Catalysts for Converting Methanol into Propylene

Control of the proximity of bifunctional zeolite@Al2O3 catalysts for efficient methanol conversion into hydrocarbons

Influence of framework Al distribution in HZSM-5 channels on catalytic performance in the methanol to propylene reaction

Facile synthesis of hierarchical H-[B]-ZSM-5 aggregates via design-optimized desilication for enhanced methanol-to-propylene conversion

Optimization of Conditions for Preparation of ZSM-5@silicalite-1 Core–shell Catalysts Via Hydrothermal Synthesis

Solvent-free and Mesoporogen-free Synthesis of Mesoporous Aluminosilicate ZSM-5 Zeolites with Superior Catalytic Properties in the Methanol-to-Olefins Reaction

Controllable Synthesis of Nano-Zsm-5 Catalysts with Large Amount and High Strength of Acid Sites for Conversion of Methanol to Hydrocarbons

Preparation of hierarchical H-[B]-ZSM-5 zeolites by a desilication method as a highly selective catalyst for conversion of methanol to propylene

High-efficient hierarchical [B]-ZSM-5 catalyst by simultaneously using of CTAB surfactant and boron promoter for methanol to olefins reaction