Abstract:Mesoporous TiO2-Al2O3 composites with different Ti/Al molar ratios were successfully synthesized via pre-hydrolysis co-precipitation method and the corresponding NiW supported hydrotreating (HDT) catalysts were prepared via incipient wetness co-impregnation method. The effects of Ti modification on the physicochemical properties of the prepared supports and catalysts were determined by the characterization techniques such as XRD, FTIR, N2 physical adsorption–desorption, SEM-EDS, ICP-OES, NH3-TPD, H2-TPR, HRTEM and XPS. Finally, quinoline, indole and coker gas oil (CGO) were used respectively as probes to investigate the Ti modification on the hydrodenitrogenation (HDN) performances of the corresponding catalysts. The results show that the TiO2-Al2O3 samples synthesized by the pre-hydrolysis co-precipitation method achieved the level of molecular composition, and the crystalline structures, pore properties and acidity properties of the TiO2-Al2O3 supports varied with the Ti/Al molar ratios. Ti modification can modulate the interaction between the active metals and the supports (MSI), and promote the formation of more so-called “type II” NiWS active phases. Furthermore, the existence of Ti3+ species in catalysts NiW/TA1 and NiW/TA2 enhanced the sulfidation degrees of active metals and weakened the bond energy between the active metals and sulfur atoms and further promoted the formation of more coordinatively unsaturated sites (CUS). The catalytic assessment results show that the HDN activities of the catalysts were effectively improved after Ti modification and the improvement was largely due to the promotion of the cleavage of the C(sp3)-N bond of basic nitrides and the C(sp2)-N bond of non-basic nitrides. The NiW/TA1 catalyst exhibited the highest performance in the HDT process of heavy oil, with a 15.8% and 12.4% improvement in HDN rate and hydrodesulfurization (HDS) rate compared with the unmodified catalyst, respectively, which was mainly attributed to its suitable pore properties, moderate MSI, large number of CUS, moderate stacking and highest active metal sulfidation degree of the active phase.

Preparation of Supported Skeletal Ni Catalyst and Its Catalytic Performance on Dicyclopentadiene Hydrogenation

Effective Hydrogen Production from Partial Oxidation of Propane over Composite Ni/Al2O3-SiC Catalyst

Synthesis of Novel NiMo Catalysts Supported on Highly Ordered TiO2-Al2O3 Composites and Their Superior Catalytic Performance for 4,6-Dimethyldibenzothiophene Hydrodesulfurization

Effect of support texture properties on Ni-Fe/γ-Al_2O_3 catalyst structure and catalytic performance for CO methanation

Role of the Solvent Evaporating Temperature on the NiMo/TiO2-Al2O3 Catalyst and the Hydrodesulfurization Performance for 4,6-Dimenthyldibenzothiophehe

Preparation of supported palladium catalyst from hydrotalcite-like compound for dicyclopentadiene resin hydrogenation

Supported Ni Catalysts: Simple Vapor Deposition Preparation Method and Improved Catalytic Performance for Oxidative Dehydrogenation of Ethane

Preparation of Raney Ni Catalyst and Research on Its Catalytic Hydrogenation Performance for Alkenyl Aromatics

Sn Modified Carbon Support PdCo Bimetallic Oxide for Boosting Low-Temperature Dehydrogenation of Dodecahydro-N-ethylcarbazole

Efficient Ni2P /Al2O3 hydrodesulfurization catalysts from surface hybridization of Al2O3 particles with graphite-like carbon

Synthesis of Ni-Co Catalysts Supported on Flower-like MgAl Composite Oxide for Hydrogen Production by <i>n</i>-Dodecane Steam Reforming

Partial Hydrogenation of Cyclopentadiene over Amorphous NiB Alloy on Α-Alumina and Titania‐modified Α-Alumina

Improved performance of Ni/Al2O3 catalyst deriving from the hydrotalcite precursor synthesized on Al2O3 support for dry reforming of methane

Deactivation of Supported Skeletal Ni Catalyst and Effect of Regeneration Temperature on Its Catalytic Performance

Synthesis of mesoporous TiO2-Al2O3 composites supported NiW hydrotreating catalysts and their superior catalytic performance for heavy oil hydrodenitrogenation

Ni–Co–Cu Supported on Pseudoboehmite-Derived Al2O3: Highly Efficient Catalysts for the Hydrogenation of Organic Functional Groups

Structural Effects of Microcrystalline Cellulose-Derived Carbon Supports on Catalytic Performance of the Pd(OH)2/C Catalysts for the Hydrogenolytic Debenzylation of Hexanitrohexaazaisowurtzitane Derivatives

Effect of Preparation Process on Compressive Strength and Hydrogenation Performance of Raney-Ni/Al2o3 Catalyst

MOF-templated fabrication of Ni@C/g-C 3 N 4 catalyst with high-dense accessible active sites achieving dicyclopentadiene hydrogenation at ambient conditions and comprehensive mechanism insight

Preparation of highly active and hydrothermally stable nickel catalysts.

Hierarchical hollow Ni/γ-Al2O3 catalyst derived from flower-like Ni-Al layered double hydroxide with stable catalytic performance for CO2 methanation