Abstract:The development of Ni-based syngas methanation catalysts with superior thermal stability remains a formidable challenge, which typically requires the use of a high Ni loading and a recipe containing very complex components. Herein, a novel Ni catalyst using a ZnAl2O4 spinel support was designed and prepared by an isopropanol-mediated controlled hydrolysis method, which demonstrated excellent reactivity and stability toward the syngas methanation reaction. Moreover, the 35% Ni/ZnAl2O4 catalyst still maintained a high reactivity after steam treatment at 750 degrees C, while the 35% Ni/Al2O3 counterpart suffered a nearly complete loss of reactivity during such an accelerated test. The detailed characterization reveals that the drastic deactivation of Ni/Al2O3 after steam treatment is attributed to the favored formation of NiAl2O4 under the severe reaction atmosphere, resulting in the loss of active Ni. In contrast, the employment of the highly stable ZnAl2O4 support can not only inhibit the sintering of supported Ni particles due to their strong interaction but also avoid the loss of the active Ni component by preventing the formation of NiAl2O4. This work sheds light on the critical role and the intrinsic mechanism of the spinel support for the construction of the desired methanation catalysts. The mechanistic scenario revealed in this work provides an important and novel solution to overcome the deactivation problem not only useful for methanation catalysts but also valid for most other supported metal catalysts commonly used in the reaction processes that require severe reaction conditions.

Preparation of highly active and hydrothermally stable nickel catalysts.

Sol-Gel Preparation, Characterization and Hydrogenation Property of Silica Supported Ni Catalyst

Effective Hydrogen Production from Partial Oxidation of Propane over Composite Ni/Al2O3-SiC Catalyst

Nickel Nanoparticles Embedded in Porous Carbon-Coated Honeycomb Ceramics: A Potential Monolithic Catalyst for Continuous Hydrogenation Reaction

Effect of support texture properties on Ni-Fe/γ-Al_2O_3 catalyst structure and catalytic performance for CO methanation

Preparation and characterization of nickel based catalysts on silica, alumina and titania obtained by sol–gel method

Development of Highly Stable Ni-Al 2 O 3 Catalysts for CO Methanation

Preparation of Hydrothermally Stable, Basic, and Highly Active Nano Nickel Catalysts for the Hydrodeoxygenation of N,N-dimethylformamide

Formation Combined with Intercalation of Ni and Its Alloy Nanoparticles within Mesoporous Silica for Robust Catalytic Reactions

An active and stable nickel-based catalyst with embedment structure for CO2 methanation

Facile preparation of a Ni/MgAl2O4 catalyst with high surface area: enhancement in activity and stability for CO methanation

Toward High‐Performance Hydrogenation at Room Temperature Through Tailoring Nickel Catalysts Stable in Aqueous Solution

Fabrication of a novel nickel-nickel aluminate nanocomposite with improved nanoparticle dispersion

Role of Structure and Acidic Nature on Catalytic Behavior of Nickel Supported H-mordenite, H-ZSM-5, and γ–alumina Catalysts

Influence of Hydrothermal Modification on the Properties of Ni/Al2O3 Catalyst

Nickel/USY Catalyst Derived from a Layered Double Hydroxide/Zeolite Hybrid Structure with a High Hydrogenation Efficiency

High-Stability ZnAl2O4 Spinel-Supported Nickel Catalyst for High-Temperature Syngas Methanation

A simple fabrication of mineral supported Ni-NiAl2O4 nanocomposites with a novel transition layer

Partial Oxidation Of Methane To Syngas Over Ni-Based Catalysts

Highly Dispersed Nickel-Containing Mesoporous Silica With Superior Stability In Carbon Dioxide Reforming Of Methane: The Effect Of Anchoring

CO Methanation over Ni/SiO2 Catalyst Prepared by Ammonia Impregnation and Plasma Decomposition