Abstract:Novel anti-dripping polyethylene terephthalate (PET) fabrics were successfully prepared by two-step gamma radiation-induced grafting polymerization of glycidyl methacrylate (GMA)/divinylbenzene (DVB) and dimethyl vinylphosphonate (DMVP) onto the surface of PET fabrics. The grafting yield increased with the increase of absorbed dose; under the absorbed dose of 21 kGy and 200 kGy, it reached 105.9% and 10.2% for GMA/DVB and DMVP, respectively. Similarly, it was noted that the grafting yield increased with monomer concentration while decreased with the dose rate. Moreover, it was confirmed by FTIR, XPS and TGA analyses that PET fabrics had been successfully modified. FTIR result showed the characteristic vibration absorption peaks of epoxy group and P-O for modified PET at 905 and 1041 cm(-1), respectively. Through XPS, the characteristic peaks of phosphorus were recognized, including P2s and P2p. TGA experiment indicated that after PDMVP grafting, thermal stability of the fabric was enhanced by the introduced phosphorus and also the formed protecting carbon layer. Compared with original PET fabrics, the tensile strength of modified PET fabrics was increased by 0.79 kN/m and 0.82 kN/m for grafting of PGMA/DVB and PDMVP, and their elongation at break increased by 11.68% and 9.69%, respectively. The results indicated that the mechanical properties of modified PET fabrics were improved at a certain extent. Additionally, the performance of anti-dripping was improved remarkably after radiation modification due to the introduction of crosslinking network and phosphorus-containing PDMVP chain. The time of per droplet generation during the combustion of PET was 3.0 s/n, and that of PET-g-PGMA/DVB was 17.0 s/n; there was no droplet after further grafting of PDMVP. The morphologies of PET fabrics before and after radiation modification as well as after combustion were observed by SEM and it was found that the modified PET fabrics by grafting of PGMA/DVB and PDMVP retained the fabric structure after combustion.

Surface Treatment of Poly(Ethylene Terephthalate) by Gamma-Ray Induced Graft Copolymerization of Methyl Acrylate and Its Toughening Effect on Poly(Ethylene Terephthalate)/Elastomer Blend

Poly(ethylene 2,5-Furandicarboxylate-mb-poly(tetramethylene Glycol)) Multiblock Copolymers: from High Tough Thermoplastics to Elastomers

Toughening of Poly(ethylene Terephthalate) and Optimizing of the Compatibilization Between PET and EPDM by Functionalized EPDM

Application of Macromolecular Chain Extender and Contribution to the Toughening of Poly(Ethylene Terephthalate)

Fabrication of poly(ethylene terephthalate)/polypropylene-based elastomer blends with balanced stiffness-toughness: The effect of reactive compatibilization

Preparation and Properties of Poly(Ethylene Terephthalate)/Poly(Butylene Terephthalate) Alloys with High Toughness

Graft Copolymerization Of Methyl Acrylate Onto PET Initiated By Potassium Diperiodatonickelate (IV)

Reactive extrusion of post‐irradiated poly(ethylene terephthalate) to improve the interfacial interactions in compounding with its immiscible polyethylene blends

Radiation Grafting of Glycidyl Methacrylate and Divinylbenzene Onto Polyethylene Terephthalate Fabrics for Improving Anti-Dripping Performance

Preparation and Properties of Poly(ethylene glycol-co-cyclohexane-1,4-dimethanol terephthalate)/Polyglycolic Acid (PETG/PGA) Blends

Study of polypropylene/polyethylene terephthalate blends compatibilized with polypropylene double‐grafted maleic anhydride and epoxy resin

Molecular dynamics simulation and experimental study on the mechanical properties of PET nanocomposites filled with CaCO 3 , SiO 2 , and POE- g -GMA

Anti-dripping PET Fabrics Prepared by Two Steps Radiation-induced Grafting

Influence of the Degree of Grafting on the Morphology and Mechanical Properties of Blends of Poly(butylene Terephthalate) and Glycidyl Methacrylate Grafted Poly(ethylene‐co‐propylene) (EPR)

Mutual Nucleating and Crystallization Behavior of Poly (ethylene Terephthalate)/polyamide 66 Blends

Toughening of poly(butylene terephthalate) with epoxidized ethylene propylene diene rubber

Surface modification of poly(ethylene terephthalate) (PET) film by gamma-ray induced grafting of poly(acrylic acid) and its application in antibacterial hybrid film

Influence of Different Molecular Weights and Concentrations of Poly(glycidyl methacrylate) on Recycled Poly(ethylene terephthalate): A Thermal, Mechanical, and Rheological Study

Polyacrylate Decorating Poly(ethylene terephthalate) (PET) Film Surface for Boosting Oxygen Barrier Property

Design of super-toughened, heat-resistant and antistatic polyethylene terephthalate-based blend composites by constructing a tenacious interface

Efficient Approach for Direct Robust Surface Grafting of Polyethyleneimine onto a Polyester Surface during Moulding