Abstract:Subzone tensile tests were used to quantitatively study the tensile properties along the equal toughness welded joint of a 30Cr2Ni4MoV steel ultra-supercritical steam turbine rotor. The results show that the weld metal (WM) has lower strength than the base metal (BM) but similar plasticity and work hardening properties; the heterogeneous microstructure of the heat-affected zone (HAZ) results in a gradient distribution of tensile properties. By fitting the stress-plastic strain curve based on the Hollomon equation, there are two hardening exponents n 1 and n 2 in each subzone of the welded joint. Based on the K–M curve of the hardening rate, during uniform plastic deformation before necking, the coarse-grained HAZ (CGHAZ) only experienced two work hardening stages III and IV, and other micorregions of the welded joint exhibited three work hardening stages III ~V. The exponent n 1 represents initial hardening stage III when the plastic strain is less than 0.003, and n 2 represents hardening stages IV~V when the plastic strain is greater than 0.003. The uneven distribution of the exponent n 2 along the joint is related to the differences in the microstructure (tempered martensite or bainite) and carbides. Observing the subzone specimens after tensile testing by TEM, it can be found that dislocation cells appeared in the tempered bainite matrix, which had better work hardening capability than tempered martensite. The lath martensite and granular bainite mixed microstructure and fine granular martensite are beneficial for improving the hardening capabilities and delaying the hardening period, but the carbides distributed in the high-angle grain boundaries are not conducive to strain hardening. The microstructure type, grain size and carbides dispersed in the matrix are the main factors affecting the hardening behavior of each subzone of the joint. The strength prediction model of welded joint subzones based on the hardness and the hardening exponent was established.

Effect of microstructure on strain hardening and strength distributions along a Cr–Ni–Mo–V steel welded joint

The Effect of Microstructure and Welding-Induced Plasticity on the Strength of Ni–Mo–Cr Alloy Welds

The Effect of Microstructure on the Fatigue Crack Growth Behavior of Ni-Cr-Mo-V Steel Weld Metal

Effect of Microstructure on Local Strain Hardening Behavior along an Equal Toughness Matching Welded Joint of a 30cr2ni4mov Welded Rotor

Effect of Long-Term Aging on Microstructure and Local Behavior in the Heat-Affected Zone of a Ni–Cr–Mo–V Steel Welded Joint

Insights into microstructure evolution and fracture mechanisms of welded joints of high strength steel patchwork components

Microstructural Evolution along the NiCrMoV Steel Welded Joints Induced by Low-Cycle Fatigue Damage

Mixed Mode Fatigue Crack Growth Behavior of Ni-Cr-Mo-V High Strength Steel Weldments

Numerical and experimental study on thermal-metallurgical-mechanical behavior of high-strength steel welded joint

The Influence of Heterogeneous Microstructure on Low-Cycle Fatigue Behavior in NiCrMoV Welded Joint

Effect of Microstructure on High-Strength Low-Alloy Steel Welded Joint Toughness with Simulation of Heat-Affected Zone Coarse-Grained Area

Evaluation of the Microstructure Related Strength of CrMoV Weldment by Using the In-Situ Tensile Test of Miniature Specimen

Crucial Microstructural Features to Determine the Mechanical Properties of Welded Joints in a Cu-Containing Low-Carbon Low-Alloy Steel After Postweld Heat Treatment

Low-cycle Fatigue Behaviors of a New Type of 10% Cr Martensitic Steel and Welded Joint with Ni-based Weld Metal

The Effect of Ferrite Phases on the Micromechanical Response and Crack Initiation in the Intercritical Heat-Affected Zone of a Welded 9cr Martensitic Steel

Effect of microstructure heterogeneity on the mechanical properties of friction stir welded reduced activation ferritic/martensitic steel

Low Cycle Fatigue Properties of a 9–12% Cr Martensitic Steel Welded Joint with Ni-based Weld Metal Based on a Local Strain Approach

Local Strain Hardening Behavior in a Dissimilar Metal Welded Joint with Buttering Layer of Ultra-Supercritical Turbine Rotor

The Effect Of The Variation Of Microstructure In The Friction Stir Welded Zone On The Strain And Tensile Properties Of Al2139

The Influence of Microstructure Evolution in Thick Plate 9%ni Steel Submerged Arc Welding Joint on Fracture Toughness Properties

Microstructure-dependent mechanical properties of an electron beam welded Ni-Co based superalloy