Abstract:This study deals with the effect of conventional sintering and microwave sintering on the densification kinetics of Titanium Carbide (TiC) in the presence of Ni (1, 1.5, 2 wt%). TiC compacts were obtained after uniaxial pressing of powders synthesised by ball milling of Titanium and Carbon and sintering was done in the presence of Nickel. The samples prepared were subjected to conventional as well as microwave sintering. The XRD and SEM analysis were used for a study of the reaction of Ti and C powders upon addition of Ni, which reduced the sintering temperature to 1200 °C. The densification of TiC powders was due to the Ti-Ni eutectic system, the liquid phase formed at this temperature assisting the sintering process. The SEM images revealed the flake like structure of TiC in which the carbon diffused into Ti upon the addition of Ni, thereby supporting enhanced mass transfer. The XRD pattern showed the presence of Titanium Oxide (TiO2) along with TiC which resulted in non-uniform distribution of hardness. Maximum hardness was achieved in the conventional sintered compacts which gradually increased with increase in Ni addition. The presence of the oxide phase and the formation of micro cracks resulted in non-uniform hardness for microwave sintered compacts. The maximum hardness of conventional sintered compact (375 HLD) was nearly 1.5 times more than the maximum hardness of the microwave sintered compact (250 HLD). The density of the microwave sintered compact was found to be higher by 8% than with the conventionally sintered compact.

Mechanochemical Synthesis of Ti(C,N) Nanopowder from Titanium and Melamine

Mechanosynthesis Mechanism of Tic Powders

Mechanochemically assisted synthesis of titanium carbonitride from metal and organic precursor

Preparation of ti-al based nanophase composite powder by mechanical alloying

Preparation of Ti/Al based nanophase composite powder by mechanical alloying

In-situ Synthesis of Nanocrystalline TiC Powders, Nanorods, and Nanosheets in Molten Salt by Disproportionation Reaction of Ti(II) Species

Studied on the Synthesize of Carbon and Nitrogen Compounds with Microwave

TiB2/TiC nano-composite powder fabricated via high energy milling

Synthesis of Si, N co-Doped Nano-Sized TiO2 with High Thermal Stability and Photocatalytic Activity by Mechanochemical Method

Synthesis of transition metal carbide nanoparticles through melamine and metal oxides

Synthesis and Characterization of Nano-sized Nitrogen Doped TiO2 by Mechanochemical Method

Photocatalytic Activity of Nitrogen Doped Nano-titanias and Titanium Nitride towards Methylene Blue Decolouration

Synthesis of Ti(C,N) Powder Via CRN Method from Rutile/Carbon Mixtures

Synthesis and Formation Mechanism of W/TiC Composite Powders by a Wet Chemical Route

Combustion Synthesis of Ti(C,N) Powder

Investigation of TiC formation during ball-milling of elemental titanium and carbon

Preparation of Nano-Sized Nitrogen-Doped TiO2 by Mechanochemical Method and Its Photocatalytic Activity

Preparations of Titanium Nitride, Titanium Carbonitride and Titanium Carbide Via a Two-Step Carbothermic Reduction Method

Preparation and Sinterability of Submicron Titanium Carbide Powders Synthesized with Phenolic Resin As Carbon Source by Carbothermal Reduction

Direct Synthesis of Controllable Microstructures of Thermally Stable and Ordered Mesoporous Crystalline Titanium Oxides and Carbide/Carbon Composites

Submicron Ti(C,N)-based cermets with improved microstructure using high-energy milled and subsequent heat-treated ultrafine Ti(C,N) powders