Abstract:Porous carbons play a vital role in supercapacitor electrodes. The capacitive performance of porous carbons depends mostly on the pore structure and surface chemistry. It is highly desirable to develop robust methods to prepare porous carbons with controlled structures and compositions. Herein, a nitrogen-doped carbon foam was prepared on the basis of polyacrylamide gel with K2CO3 and K2B4O7 as the activating agent and salt template, respectively. Due to the constraint effect of the cross-linked polyacrylamide network, K2CO3 and K2B4O7 can be homogeneously embedded in the polymer matrix. The subsequent carbonization results in the nitrogen-doped carbon foam (PACF) with a hierarchically porous structure and high specific surface area (∼3404.8 m2 g–1). K2B4O7 not only serves as the soluble salt template but can also reinforce the carbonaceous skeleton during carbonization. PACF yields an outstanding specific capacitance (346.9 F g–1 at 0.5 A g–1), good rate performance (224.4 F g–1 at 50 A g–1), and excellent cycle capability (retaining 97.2% of the initial capacitance after 10,000 consecutive charge–discharge cycles). This study demonstrates the potential of polyacrylamide gel as a promising carbon precursor and enriches the tool box for the preparation of porous carbons.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsaem.1c00777?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsaem.1c00777</a>.Appearances of the prepared PAM gel-derived carbons, photograph of mechanical properties, SEM images, nitrogen physisorption results, histogram of percentages of different nitrogen species, structure characterization, electrochemical performances, elemental concentrations, electrochemically active surface area determination method (<a class="ext-link" href="/doi/suppl/10.1021/acsaem.1c00777/suppl_file/ae1c00777_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Preparation of nitrogen-doped macro-/mesoporous carbon foams as electrode material for supercapacitors

Synthesis and Electrochemical Properties of Macro-/Microporous Carbon Foams

Synthesis and Electrochemical Performance of Mesoporous Carbon Foams by Microemulsion Method

Nitrogen-functionalized Microporous Carbon Nanoparticles for High Performance Supercapacitor Electrode

Nickel-doped activated mesoporous carbon microspheres with partially graphitic structure for supercapacitors

Highly N/O co-doped ultramicroporous carbons derived from nonporous metal-organic framework for high performance supercapacitors

Nitrogen-containing ultramicroporous carbon nanospheres for high performance supercapacitor electrodes

Facile Synthesis of Nitrogen-Doped Microporous Carbon Spheres for High Performance Symmetric Supercapacitors

Polyacrylamide Gel-Derived Nitrogen-Doped Carbon Foam Yields High Performance in Supercapacitor Electrodes

Nitrogen-Doped Activated Carbons Derived From A Co-Polymer For High Supercapacitor Performance

Nitrogen Doped Macroporous Carbon As Electrode Materials For High Capacity Of Supercapacitor

Facile synthesis of microporous N-doped carbon material and its application in supercapacitor

Microporous MOFs Engaged in the Formation of Nitrogen-Doped Mesoporous Carbon Nanosheets for High-Rate Supercapacitors

Preparation of N-doped mesoporous carbons for supercapacitor

Epoxy coated melamine-foam used to synthesize nitrogen-doped microporous carbon for super-capacitive energy storage

Nitrogen-doped micro-nano carbon spheres with multi-scale pore structure obtained from interpenetrating polymer networks for electrochemical capacitors

Fluorine and nitrogen co-doped mesoporous carbon derived from polytetrafluoroethylene@melamine sponge for supercapacitor application

High Performance Aqueous Supercapacitor Based on Highly Nitrogen-Doped Carbon Nanospheres with Unimodal Mesoporosity

Nitrogen-doped porous carbon derived from biomass waste for high-performance supercapacitor

High-surface-area and high-nitrogen-content carbon microspheres prepared by a pre-oxidation and mild KOH activation for superior supercapacitor

Aminal/Schiff‐Base Polymer to Fabricate Nitrogen‐Doped Porous Carbon Nanospheres for High‐Performance Supercapacitors