Abstract:A series of nitrogen-containing polymer and carbon spheres were obtained by the sol-gel method. In particular, the nitrogen-rich carbon spheres were prepared by one-pot hydrothermal synthesis in the presence of resorcinol/formaldehyde as carbon precursors and ethylenediamine (EDA) as both a base catalyst and nitrogen precursor, followed by carbonization in nitrogen and activation with CO2. The introduction of EDA to the sol gel system resulted in structurally bonded nitrogen-containing carbon spheres. The nitrogen doping level and the particle size can be tuned by varying the EDA amount in the reaction mixture. The maximum nitrogen doping level of 7.2 wt % in carbon spheres could be achieved without sacrificing the spherical morphology. The diameter of these carbon spheres (CS) can be tuned in the rage of 50-1200 nm by varying the EDA amount. N-2 adsorption analysis showed that the aforementioned activated carbon spheres exhibited high surface area reaching up to 1224 m(2)/g. Ultra high CO2 adsorption capacities, 4.1 and 6.2 mmol/g, corresponding to an equilibrium pressure of I bar, were measured on nitrogen-containing activated carbon spheres at 25 and 0 degrees C, respectively. Electrochemical measurements performed on these carbon spheres for double layer capacitors showed very high capacitance up to similar to 388 F/g at 1.0 A/g, outstanding rate capability (60% capacitance retention at 100 A/g), and unprecedented cycling stability (similar to 98% capacitance retention even after 8000 cycles) in 1 M H2SO4 electrolyte solution.

Nitrogen-doped micro-nano carbon spheres with multi-scale pore structure obtained from interpenetrating polymer networks for electrochemical capacitors

Nitrogen-containing carbon microspheres for supercapacitor electrodes

Nitrogen-functionalized Microporous Carbon Nanoparticles for High Performance Supercapacitor Electrode

Nitrogen-Enriched Hollow Porous Carbon Nanospheres with Tailored Morphology and Microstructure for All-Solid-State Symmetric Supercapacitors

Preparation of nitrogen-doped macro-/mesoporous carbon foams as electrode material for supercapacitors

Carbon-coated mesoporous NiO nanoparticles as an electrode material for high performance electrochemical capacitors

Nitrogen-Containing Microporous Carbon Nanospheres with Improved Capacitive Properties

N-doped Carbon Hollow Microspheres for Metal-Free Quasi-Solid-state Full Sodium-Ion Capacitors

Molecular Engineering Of Supercapacitor Electrodes With Monodispersed N-Doped Carbon Nanoporous Spheres

Aminal/Schiff‐Base Polymer to Fabricate Nitrogen‐Doped Porous Carbon Nanospheres for High‐Performance Supercapacitors

Preparation and Properties of N-Doped Carbon Microtubes As the Electrode Material in Electrochemical Capacitor

Nitrogen-doped hollow carbon polyhedron derived from metal-organic frameworks for supercapacitors

N/P co-doped porous carbon microspheres for supercapacitor with long-term electrochemical stability

Nitrogen enriched porous carbon spheres: attractive materials for supercapacitor electrodes and CO2 adsorption

Activated Porous Carbon Spheres with Customized Mesopores Through Assembly of Diblock Copolymers for Electrochemical Capacitor

Nitrogen Doped Macroporous Carbon As Electrode Materials For High Capacity Of Supercapacitor

Highly Nitrogen and Sulfur Dual-Doped Carbon Microspheres for Supercapacitors

Nitrogen-doped hollow carbon spheres from bio-inspired dopamine: Hexamethylenetetramine-induced polymerization, morphology control and supercapacitor performance

Facile Synthesis of Nitrogen-Doped Microporous Carbon Spheres for High Performance Symmetric Supercapacitors

Nitrogen Enriched Mesoporous Carbon Spheres Obtained by a Facile Method and Its Application for Electrochemical Capacitor

Core–shell N-doped Carbon Spheres for High-Performance Supercapacitors