Abstract:A series of nitrogen-doped carbons were prepared by using biomass waste sawdust as carbon source for supercapacitors. A new nitrogen-doping strategy was proposed to introduce nitrogen element into carbons by using ethylenediamine and carbon as nitrogen source through the polymerization reaction on sawdust under moderate conditions. The raw carbons were further activated with KOH to improve the surface area to increase the electric double layer capacitance while the heteroatoms can improve the pseudocapacitance. The prepared carbons were characterized with different techniques and the electrochemical performances were tested. It was found that the nitrogen-doped carbons activated with a KOH to carbon mass ratio of 5 (NC600-800-5) has the largest specific surface area (1674 m(2)g(-1)) and moderate nitrogen content (2.88 wt%). Compared with the carbon without introduction of nitrogen element (C600-800-5), the capacitive performances of nitrogen-doped carbons were greatly improved, which may be due to the increase of pseudocapacitance and the improvement of wettability introduced by nitrogen element. The largest specific capacitance, 367 F g(-1), was reached at 0.5 A g(-1 )in 6 M KOH solution while the specific capacitance of C600-800-5 is only 279 F g(-1). After 10,000 cycles at 3 A g(-1), the specific capacitance can keep 96.7% of the initial value, suggesting the excellent cycling performance. The energy density can reach 8.7 Wh Kg(-1) at a power density of 251.6 W kg(-1). Thus, it is proved that the nitrogendoping strategy is effective and the introduction of nitrogen element to carbons is particularly important to the improvement of the electrochemical performances.

Facile Synthesis of Nitrogen-Doped Microporous Carbon Spheres for High Performance Symmetric Supercapacitors

Nitrogen-functionalized Microporous Carbon Nanoparticles for High Performance Supercapacitor Electrode

Synthesis of MnO2/N-doped Ultramicroporous Carbon Nanospheres for High-Performance Supercapacitor Electrodes

Cooking Carbon with Protic Salt: Nitrogen and Sulfur Self-Doped Porous Carbon Nanosheets for Supercapacitors

Hydrangea-like N/O codoped porous carbons for high-energy supercapacitors

Nitrogen-doped hollow carbon polyhedron derived from metal-organic frameworks for supercapacitors

Construction of N-Doped Hollow Carbon Nanospheres Through a Novel Self-Template Strategy As High-Performance Electrode Materials for Supercapacitors

Nitrogen-Doped Mesoporous Carbon Microspheres by Spray Drying-Vapor Deposition for High-Performance Supercapacitor

Self-Template Synthesis of Nitrogen-Doped Hollow Carbon Nanospheres with Rational Mesoporosity for Efficient Supercapacitors

Sustainable Nitrogen-Containing Hierarchical Porous Carbon Spheres Derived from Sodium Lignosulfonate for High-Performance Supercapacitors

Oxygen and Nitrogen Co‐enriched Sustainable Porous Carbon Hollow Microspheres from Sodium Lignosulfonate for Supercapacitors with High Volumetric Energy Densities

Porous Carbon Spheres Derived from Hemicelluloses for Supercapacitor Application

Nitrogen and Sulfur Codoped Porous Carbon Microsphere: a High Performance Electrode in Supercapacitor

Aminal/Schiff‐Base Polymer to Fabricate Nitrogen‐Doped Porous Carbon Nanospheres for High‐Performance Supercapacitors

Nitrogen-doped highly dense but porous carbon microspheres with ultrahigh volumetric capacitance and rate capability for supercapacitors

Biomass-derived nitrogen and sulfur co-doped sheet-like porous carbon for high-performance supercapacitors

Facile 3D Nitrogen‐Doped Hierarchical Porous Carbon for High‐Performance Supercapacitors

Facile Preparation of 2D Nitrogen and Sulfur Co-Doped Porous Carbon Nanosheets for High-Performance Supercapacitors

Facile synthesis of microporous N-doped carbon material and its application in supercapacitor

N,P,S-Codoped Hierarchically Porous Carbon Spheres with Well-Balanced Gravimetric/Volumetric Capacitance for Supercapacitors

N-doped Carbons with Hierarchically Micro- and Mesoporous Structure Derived from Sawdust for High Performance Supercapacitors