Abstract:A series of nitrogen-doped carbons were prepared by using biomass waste sawdust as carbon source for supercapacitors. A new nitrogen-doping strategy was proposed to introduce nitrogen element into carbons by using ethylenediamine and carbon as nitrogen source through the polymerization reaction on sawdust under moderate conditions. The raw carbons were further activated with KOH to improve the surface area to increase the electric double layer capacitance while the heteroatoms can improve the pseudocapacitance. The prepared carbons were characterized with different techniques and the electrochemical performances were tested. It was found that the nitrogen-doped carbons activated with a KOH to carbon mass ratio of 5 (NC600-800-5) has the largest specific surface area (1674 m(2)g(-1)) and moderate nitrogen content (2.88 wt%). Compared with the carbon without introduction of nitrogen element (C600-800-5), the capacitive performances of nitrogen-doped carbons were greatly improved, which may be due to the increase of pseudocapacitance and the improvement of wettability introduced by nitrogen element. The largest specific capacitance, 367 F g(-1), was reached at 0.5 A g(-1 )in 6 M KOH solution while the specific capacitance of C600-800-5 is only 279 F g(-1). After 10,000 cycles at 3 A g(-1), the specific capacitance can keep 96.7% of the initial value, suggesting the excellent cycling performance. The energy density can reach 8.7 Wh Kg(-1) at a power density of 251.6 W kg(-1). Thus, it is proved that the nitrogendoping strategy is effective and the introduction of nitrogen element to carbons is particularly important to the improvement of the electrochemical performances.

N-doped Carbons with Hierarchically Micro- and Mesoporous Structure Derived from Sawdust for High Performance Supercapacitors

N-doped Hierarchically Micro- and Mesoporous Carbons with Superior Performance in Supercapacitors

Nitrogen-functionalized Microporous Carbon Nanoparticles for High Performance Supercapacitor Electrode

N-Doped Porous Carbons with High Surface Areas Prepared Through One-Step Chemical Activation and Their Application for Supercapacitors

Nitrogen-doped porous carbon derived from biomass waste for high-performance supercapacitor

Nitrogen-doped Hierarchically Ellipsoidal Porous Carbon Derived from Al-based Metal-Organic Framework with Enhanced Specific Capacitance and Rate Capability for High Performance Supercapacitors

Three-dimensional Nitrogen-Doped Hierarchical Porous Carbon Derived from Cross-Linked Lignin Derivatives for High Performance Supercapacitors

Nitrogen-Doped Hierarchical Porous Carbon Nanowhisker Ensembles on Carbon Nanofiber for High-Performance Supercapacitors

Enhancing the Energy Density of Supercapacitors by Introducing Nitrogen Species into Hierarchical Porous Carbon Derived from Camellia Pollen

Nitrogen-doped carbons derived from cotton pulp for improved supercapacitors

Nitrogen-Doped Porous Carbons Derived from Peanut Shells as Efficient Electrodes for High-Performance Supercapacitors

Fabrication of high performance structural N-doped hierarchical porous carbon for supercapacitors

Chitin derived nitrogen-doped porous carbons with ultrahigh specific surface area and tailored hierarchical porosity for high performance supercapacitors

Biomass-derived nitrogen-doped porous carbons with tailored hierarchical porosity and high specific surface area for high energy and power density supercapacitors

Facile synthesis of nitrogen-enriched nanoporous carbon materials for high performance supercapacitors.

A Nitrogen-doped Hierarchical Mesoporous/Microporous Carbon for Supercapacitors

A Novel Approach for Preparing In-Situ Nitrogen Doped Carbon Via Pyrolysis of Bean Pulp for Supercapacitors

Facile Synthesis of Nitrogen Self-Doped Hierarchical Porous Carbon Derived from Pine Pollen Via MgCO3 Activation for High-Performance Supercapacitors

One pot synthesis of nitrogen-doped hierarchical porous carbon derived from phenolic formaldehyde resin with sodium citrate as activation agent for supercapacitors

Nitrogen-doped Ordered Mesoporous Carbons Based on Cyanamide As the Dopant for Supercapacitor

A Simple Method to Fabricate N-doped Hierarchical Porous Carbon for Supercapacitors