Nitrogen-doped Ordered Mesoporous Carbons Based on Cyanamide As the Dopant for Supercapacitor

Quan Shi,Renyuan Zhang,Yingying Lu,Yonghui Deng,Ahmed A. Elzatahrya,Dongyuan Zhao

DOI: https://doi.org/10.1016/j.carbon.2014.12.013

IF: 10.9

2015-01-01

Carbon

Abstract:Nitrogen-doped ordered mesoporous carbons (N-doped OMCs) with a high surface area of 1741m2/g and nitrogen content up to 15wt.% have been synthesized by nanocasting approach by using SBA-15 as a hard template, phenolic resin (resol) as a carbon source and high nitrogen-containing cyanamide as the nitrogen dopant. The introduction of cyanamide not only incorporates high-content nitrogen into the carbon matrix in the primary forms of pyridinic and quaternary species, but also greatly increases the surface area of materials. The obtained N-doped OMCs have large surface area with mesoporosity up to 92%, uniform and appropriate pore size (3.6–4.1nm), large pore volume (1.2–1.81cm3/g). These merits together with high nitrogen enrichment lead to a specific capacitance (230F/g at 0.5A/g) and good rate capability (175F/g at 20A/g with capacitance retention of 77.4%) in 6M KOH aqueous electrolytes.