Fluorine and nitrogen co-doped mesoporous carbon derived from polytetrafluoroethylene@melamine sponge for supercapacitor application

Haiyang Jia,Jingfang Zhu,Meng Zhang,Shijing Sang,Feng Hu,Fen Zhang

DOI: https://doi.org/10.1016/j.est.2021.102613

IF: 9.4

2021-06-01

Journal of Energy Storage

Abstract:<p>By using sponge composite as the precursor, a nitrogen and fluorine co-doped porous carbon is prepared <em>via</em> a chemical etching process. The specific surface area and total volume of the mesoporous carbon are 1799 m² <em>g</em>⁻¹ and 1.48 m³ <em>g</em>⁻¹, respectively. The doping amount of the fluoride and nitrogen in the resulting co-doped carbon is determined to be 1.2 at.% and 2.7 at.%, respectively. In a three-electrode system in 6 M KOH electrolyte, when mass loading of active material is 4 and 6 mg, electrodes deliver specific capacitances of 299 and 284 F <em>g</em>⁻¹ at a current density of 1 A <em>g</em>⁻¹, respectively. In a symmetric-electrode system in the same electrolyte, an electrode shows the specific capacitance of 233 F <em>g</em>⁻¹ at the same current density. In aqueous electrolyte, the assembled simulated supercapacitor reaps a maximum specific energy of 8.3 W h kg⁻¹ at a specific power of 101 W kg⁻¹. Under the current density of 5 A <em>g</em>⁻¹, after 6000 cycles, the 94.1% remaining capacitance indicates a good cycle stability. Findings demonstrate the synthesized fluorine and nitrogen co-doped porous carbon can be used as electroactive material for high-performance supercapacitor.</p>

energy & fuels