Controllable Synthesis of (nh4)fe2(po4)2(oh)·2h2o Using Two-Step Route: Ultrasonic-intensified Impinging Stream Pre-Treatment Followed by Hydrothermal Treatment.
Bin Dong,Guang Li,Xiaogang Yang,Luming Chen,George Z. Chen
DOI: https://doi.org/10.1016/j.ultsonch.2017.12.008
IF: 9.336
2018-01-01
Ultrasonics Sonochemistry
Abstract:(NH4)Fe-2(PO4)(2)(OH)center dot 2H(2)O samples with different morphology are successfully synthesized via two-step synthesis route - ultrasonic-intensified impinging stream pre-treatment followed by hydrothermal treatment (UIHT) method. The effects of the adoption of ultrasonic-intensified impinging stream pre-treatment, reagent concentration (C), pH value of solution and hydrothermal reaction time (7) on the physical and chemical properties of the synthesised (NH4)Fe-2(PO4)(2)(OH)center dot 2H(2)O composites and FePO4 particles were systematically investigated. Nano-seeds were firstly synthesized using the ultrasonic-intensified T-mixer and these nano-seeds were then transferred into a hydrothermal reactor, heated at 170 degrees C for 4 h. The obtained samples were characterized by utilising XRD, BET, TG-DTA, SEM, TEM, Mastersizer 3000 and FTIR, respectively. The experimental results have indicated that the particle size and morphology of the obtained samples are remarkably affected by the use of ultrasonic-intensified impinging stream pre-treatment, hydrothermal reaction time, reagent concentration, and pH value of solution. When such (NH4)Fe-2(PO4)(2)(OH)center dot 2H(2)O precursor samples were transformed to FePO4 products after sintering at 650 degrees C for 10 h, the SEM images have clearly shown that both the precursor and the final product still retain their monodispersed spherical microstructures with similar particle size of about 3 pm when the samples are synthesised at the optimised condition.