Abstract:Carbon coated hollow alpha-Fe2O3 spheres were prepared via a facile two-step hydrothermal method. The appearance and crystalline structure of the samples were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD) and transmission electron microscopy (TEM). The morphology showed that the hollow spheres were composed of well crystallized nanoparticles after the first hydrothermal reaction and subsequent calcinations. A thin carbon film was coated on each Fe2O3 nanoparticles after the second hydrothermal procedure. This carbon coating was probably beneficial to maintain the microstructure of the active material during repeatable lithiation and delithiation. Afterwards, the samples were assembled into half-cells to investigate the electrochemical properties. The electrode delivered relatively high initial discharge/charge capacities of 1291/890 mA h g(-1) at the rate of 0.3 C. The reversible capacity maintained very well in a prolonged 140 cycles. The capacity retention was 89% after 70 cycles, and that was 81% after 140 cycles. This exceptional lithium storage property was probably attributed to the porous and hollow structure which allowed the penetration of electrolyte to the inner of the electrode, the nanoscale Fe2O3 particles which shortened the migration pathway for lithium ion, and the carbon coating which kept the active materials structure intact. The attractive electrochemical performance suggested the carbon coated hollow Fe2O3 spheres would be the potential anode material for future lithium ion battery.

The pH Influence on the Preparation of Hollow Fe2O3 Spheres by Hydrothermal Method

Influence of NH 4 + on the preparation of carbonaceous spheres by a hydrothermal process

Synthesis and phase formation mechanism of alpha-Fe2O3 powders by hydrothermal reaction method

The Effect of pH value on the nano-particle size of bi substituted yttrium iron garnet

Hydrothermal preparation of α-Fe2O3 nano-scale spheres and their photocatalytic property study

Influence of pH Value on Crystal Structure and Microstructure of Aluminum Hydroxide

pH control on preparation of nano-TiO_2 by gel-sol process

Preparation and Characterization of Silver Coated Hollow SnO2 Sphere with Open Structure

Investigating the effect of pH on the growth of coprecipitated Ni0.8Co0.1Mn0.1(OH)2 agglomerates as precursors of cathode materials for Li-ion batteries

Effect of pH on the microstructure and magnetic properties of Cu0.2Co0.8Fe2O4 synthesized by sol–gel method

Controlled Synthesis of Porous FeCO3 Microspheres and the Conversion to Α-Fe2o3 with Unconventional Morphology

Nonstoichiometric M-ferrite Porous Spheres: Preparation, Shape Evolution and Magnetic Properties

Synthesis of Monodisperse and Single-Crystal Fe3o4 Hollow Spheres by A Solvothermal Approach

Preparation of Spherical Fepo4 Cathode Material for Lithium Ion Batteries

Formation Mechanism and Magnetic Properties of Hollow Fe3o4 Nanospheres Synthesized Without Any Surfactant

Synthesis and Characterization of Hollow Alpha-Fe2o3 Spheres with Carbon Coating for Li-Ion Battery

Preparation and Characterization of SnO2 Hollow Spheres and Their Carbon-coated Composites

Synthesis of size-controlled hollow Fe<sub>3</sub>O<sub>4</sub> nanospheres and their growth mechanism

Preparation ofα-Fe2O3 nanoparticles by hydrolysis precipitation method

Research on Preparation of Nano-porous Lithium Iron Phosphate for Lithium-ion Battery Electrode Materials

Influence of Ph on the Morphology of Yttrium Oxide Hydroxide Nitrate Nanocrystal