Abstract:Hollow structured magnetite spheres were fabricated by a simple solvothermal process, with the assistance of various ammonium salts, where ethylene glycol was used as the solvent and reducing agent. The results of X-ray diffraction, scanning electron microscopy and transmission electron microscopy show that the as-synthesized products are pure single-phase Fe3O4 with good crystalline state, and all the samples are hollow structures except for the S-d sample, which was obtained by the assistance of NH4HCO3. The X-ray photoelectron spectrometry manifests that the Fe3+ ions on the surface of the hollow spheres exist in the form of Fe3O4, and Mossbauer measurements reveal that the hollow spheres are similar to the stoichiometric Fe3O4. The possible formation mechanism of hollow magnetite spheres with various sizes was discussed in detail. Meanwhile magnetic properties were determined by using a vibrating sample magnetometer at room temperature. The magnetic properties investigation showed that the Fe3O4 spheres were ferromagnetic with small hysteresis loops. The values of saturation magnetization are 82.989, 78.049 and 87.417 emu g(-1) for the S-a, S-b and S-c samples, which decreases with increasing particle size. This phenomenon may be caused by the content of Fe3+ on A- and B-sites of the spinel ferrite. Based on experimental results, the relationship between their microcomponents also has been studied.

Synthesis of Monodisperse and Single-Crystal Fe3o4 Hollow Spheres by A Solvothermal Approach

Synthesis of Monodispersed Fe3O4 Magnetite Nanoparticles by ethylene glycol solvothermal method

Synthesis and Characterization of Monodisperse Fe3O4Nanospheres with Uniform Particle Size Distribution by a Simple Solvothermal Method

Formation Mechanism and Magnetic Properties of Hollow Fe3o4 Nanospheres Synthesized Without Any Surfactant

Solvothermal Synthesis and Magnetic Property of Monodispersed Fe_3O_4 Nano-powders

Monodisperse Fe 3 O 4 spheres: Large-scale controlled synthesis in the absence of surfactants and chemical kinetic process

The Oriented Self‐Assembly of Magnetic Fe3O4 Nanoparticles into Monodisperse Microspheres and Their Use As Substrates in the Formation of Fe3O4 Nanorods

Facile Synthesis and Characterization of ZnFe2O4/α-Fe2O3 Composite Hollow Nanospheres

Solvothermal synthesis, characterization and formation mechanism of single-crystalline SrTiO3 dense spheres with monoethanolamine as reaction medium solvent

Microwave-assisted Solution-Phase Preparation and Growth Mechanism of FeMoO4hierarchical Hollow Spheres

A simple solvothermal synthesis and characterization of round-biscuit-like Fe3O4 nanoparticles with adjustable sizes

Preparation and Surface Modification of Monodisperse Fe3O4 Nanoparticles

Controlled Synthesis of Fe3O4 Single Crystalline Spheres in One Solvothermal System and Their Application in MRI

A novel synthesis of hollow Fe3O4 nanorods with a high saturation magnetization

Ferromagnetic Fe3O4 Nanofibers: Electrospinning Synthesis and Characterization

A Facile Solvothermal Synthesis of Octahedral Fe3 O4 Nanoparticles.

Shape Evolution and Tunable Properties of Monodisperse Magnetite Crystals Synthesized by a Facile Surfactant‐Free Hydrothermal Method

Synthesis of N-Hexadecylphosphonic Acid-Coated Monodisperse Fe3O4 Superparamagnetic Nanoparticles

Magnetic Monodisperse Fe3o4 Nanoparticles

A Novel Method for the Fabrication of Monodisperse Hollow Silica Spheres

Investigation of the Solvothermal Method for Fabrication of Magnetite Microcrystals