Abstract:Hollow structured magnetite spheres were fabricated by a simple solvothermal process, with the assistance of various ammonium salts, where ethylene glycol was used as the solvent and reducing agent. The results of X-ray diffraction, scanning electron microscopy and transmission electron microscopy show that the as-synthesized products are pure single-phase Fe3O4 with good crystalline state, and all the samples are hollow structures except for the S-d sample, which was obtained by the assistance of NH4HCO3. The X-ray photoelectron spectrometry manifests that the Fe3+ ions on the surface of the hollow spheres exist in the form of Fe3O4, and Mossbauer measurements reveal that the hollow spheres are similar to the stoichiometric Fe3O4. The possible formation mechanism of hollow magnetite spheres with various sizes was discussed in detail. Meanwhile magnetic properties were determined by using a vibrating sample magnetometer at room temperature. The magnetic properties investigation showed that the Fe3O4 spheres were ferromagnetic with small hysteresis loops. The values of saturation magnetization are 82.989, 78.049 and 87.417 emu g(-1) for the S-a, S-b and S-c samples, which decreases with increasing particle size. This phenomenon may be caused by the content of Fe3+ on A- and B-sites of the spinel ferrite. Based on experimental results, the relationship between their microcomponents also has been studied.

Microwave-assisted Solution-Phase Preparation and Growth Mechanism of FeMoO4hierarchical Hollow Spheres

Self-assembled Flower-Like Hierarchical Spheres and Nanobelts of Manganese Oxide by Hydrothermal Method and Morphology Control of Them

Synthesis of Monodisperse and Single-Crystal Fe3o4 Hollow Spheres by A Solvothermal Approach

Microwave Fabrication and Magnetic Property of Hierarchical Spherical Α-Fe2o3 Nanostructures

Synthesis and Characterization of Monodisperse Fe3O4Nanospheres with Uniform Particle Size Distribution by a Simple Solvothermal Method

Pancake-like Fe2(MoO4)3 Microstructures: Microwave-Assisted Hydrothermal Synthesis, Magnetic and Photocatalytic Properties

Tungstenic acid induced assembly of hierarchical flower-like MoS2 spheres

Pancake-like Fe 2 ( MoO 4 ) 3 Microstructures : Microwave-Assisted Hydrothermal Synthesis , Magnetic and Photocatalytic Properties W

Formation Mechanism and Magnetic Properties of Hollow Fe3o4 Nanospheres Synthesized Without Any Surfactant

Monodisperse Fe 3 O 4 spheres: Large-scale controlled synthesis in the absence of surfactants and chemical kinetic process

The Oriented Self‐Assembly of Magnetic Fe3O4 Nanoparticles into Monodisperse Microspheres and Their Use As Substrates in the Formation of Fe3O4 Nanorods

Synthesis, Characterization and Photocatalytic Activity of Hierarchical Spherical TiO2 Nanostructures

Hierarchical FeWO4 Microcrystals: Solvothermal Synthesis and Their Photocatalytic and Magnetic Properties

A facile method to fabricate porous Co3O4 hierarchical microspheres

Formation of Uniform Fe3O4 Hollow Spheres Organized by Ultrathin Nanosheets and Their Excellent Lithium Storage Properties

Hierarchical Fe3O4@TiO2 yolk-shell microspheres with enhanced microwave-absorption properties.

Synthesis of Single Crystal CdMoO4 Octahedral Microparticles Via Microemulsion-Mediated Route.

Achieving Hierarchical Hollow Carbon@Fe@Fe3o4 Nanospheres with Superior Microwave Absorption Properties and Lightweight Features

Hydrothermal synthesis and characterization of α-FeOOH and α-Fe2O3 uniform nanocrystallines

Facile Synthesis and Characterization of ZnFe2O4/α-Fe2O3 Composite Hollow Nanospheres

Assembly of MOFs/polymer hydrogel derived Fe3O4-CuO@hollow carbon spheres for photochemical oxidation: Freezing replacement for structural adjustment