Highly Surface-Roughened Quasi-Spherical Silver Powders in Back Electrode Paste for Silicon Solar Cells
Peng Yin,Shouchao Liu,Qiuying Li,Xiaolei Chen,Weihong Guo,Chifei Wu
DOI: https://doi.org/10.1088/2053-1591/aa827d
IF: 2.025
2017-01-01
Materials Research Express
Abstract:In our work, highly surface-roughened quasi-spherical silver powders with controllable size and superior dispersibility, which have narrow size distribution and relatively high tap density, were successfully prepared by reducing silver nitrate with ascorbic acid in aqueous solutions. Gum arabic (AG) was selected as dispersant to prevent the agglomeration of silver particles. Furthermore, the effects of preparation conditions on the characteristics of the powders were systematically investigated. By varying the concentration of the reactants, dosage of dispersant, the feeding modes, synthesis temperature and the pH value of the mixture solution of silver nitrate and AG, the resulted silver particles displayed controllable size, different morphologies and surface roughness. The spherical silver powder with mean particle size of 1.20 mu m, tap density of 4.1 g cm(-3) and specific area value of 0.46 m(2) g(-1) was prepared by adjusting preparation conditions. The AG absorbed on the surface preventing the silver particles from diffusion and aggregation was proved by the ultraviolet spectra. Observations of SEM images showed that the as-prepared silver powders were relatively monodisperse silver spheres with highly roughened surface and the particle size was controllable from 1 mu m to 5 mu m, specific surface area value from approximately 0.2 m(2) g(-1) to 0.8 m(2) g(-1). X-ray diffraction (XRD) patterns, energy dispersive spectroscopy (EDS), x-ray photoelectron spectra (XPS) and thermal gravity analysis (TGA) demonstrated high crystallinity and purity of the obtained silver powders.