Abstract:Two kinds of adsorbates—L-ascorbic acid and NaOH were used separately to investigate the effects of adsorbate distribution between ethanol bulk phase and the phase of water-rich layer adsorbed by the surface of SiO2 particles on the preparation of silver nanoparticles on SiO2 particles. When the adsorbate L-ascorbic acid was used, L-ascorbic distributes mainly in the ethanol bulk phase and thus the Ag particle generating reaction will take place in the ethanol bulk phase with the generated Ag particle size of about 18 nm. When the adsorbate NaOH was used, NaOH distributes mainly in the phase of water-rich layer adsorbed on the surface of SiO2 particles and thus the Ag particles generate in the water-rich adsorption layer with particle size of only about 5.4 nm. Since the NaOH concentration effects its distribution between the two phases of ethanol bulk phase and water-rich adsorption layer, the further experiments with changing NaOH concentration in the reaction system from 0.0170 to 0.404 g·L-1 were conducted. Results show that when concentration of NaOH in the system was increased from 0.0170 to 0.135 g·L-1, the NaOH concentration in the water-rich adsorption layer increases with the increase of NaOH concentration in the system gradually, which causes the generation of Ag grains gradually centralizes in the adsorption layer with the grain size decreases from 8 nm to 5 nm, and the Ag particles generated cover the SiO2 more uniformly. When NaOH concentration in the system was increased from 0.135 to 0.404 g·L-1, the amount of NaOH in the system is over the maximum NaOH capacity that can be contained in the water-rich adsorption layer and thus the NaOH concentration in ethanol bulk phase will increase to the limit, above which, the Ag generating reaction rate in it will accelerate more quickly than that in the water-rich adsorption layer, which causes the main generation zone of silver nanoparticles moves from water-rich adsorption layer to ethanol bulk phase gradually, and at the same time, the generated Ag grain size will increase from 5 nm to 12 nm.

Study on the factors affecting the morphology of silver powder in liquid phase chemical reduction

Study on the influence factors of silver powders size was prepared by liquid-phase reduction method

Study on Preparation of High-Performance Flake Silver Powder by Liquid Phase Reduction

The effect of reaction factors on the morphology of silver particles prepared by chemical reduction method

Preparation and Microstructure of Silver Nanopowder with Spheric Morphology

Preparation and Characterization of Silver Powders with Spheric Shape and Different Sizes

Study on the tap density of silver powder prepared by liquid phase reduction method

Effect of Interphase Distribution of Reactants in Binary Liquids on Preparation of Silver Nanoparticles on Silica Particles

Influence of adsorption of reactants on preparation of silver nanoparticles by adsorption phase synthesis

Preparation of Ultrafine Silver Powder by Reduction of Glucose

Preparation of Micron Silver Powder by Multistep Reduction and Its Crystal Growth Characteristics

Study on Preparation of Size-Controllable Spherical Ag Powders with High Tap Density

Progress in Preparation of Ultrafine Copper Powder by Chemical Reduction Method

Synthesis of Silver Nanocubes and Factors Affecting the Size and Shape of Sliver Nanoporticles

Preparation of Ag-Al2O3 nano-composites powder

Preparation of AgSnO2 Nano-Composite Powder by Wet Chemical Method

Preparation and Characterization of Silver Coated Hollow SnO2 Sphere with Open Structure

Preparation of AgSnO_2 nano-composite powder by wet chemical method

Morphology and Composition Controlled Synthesis of Flower-Like Silver Nanostructures.

Effects of Surfactants on Dispersive Performance of Ultrafine Silver Powder

Synthesis of nanosized silver particles by chemical reduction method