Abstract:Hot pressing was used to produce compact ceramic samples with the following composition (wt.%): 60 ZrB2 + 20 SiC + 20 (Al2O3 + 32 t-ZrO2). The tetragonal modification of zirconium oxide in the eutectic was stabilized by yttrium oxide. The porosity of the samples was 3–5%. The mechanical properties of the ceramics (hardness HV, fracture toughness KIc, tensile strength δf, compressive strength Y, grain-boundary strength S, and bending strength σ) were studied. Analysis of the microstructure and elemental composition of the phases revealed that a defect-free structure developed in the ZrB2-based composite through strong Van Der Waals adhesive interaction at the SiC–Al2O3 interface, which increased the fracture toughness to 9.4 MPa ∙ m1/2. In turn, this increased the grain strength from 0.64 GPa for the basic composite to 3.46 GPa for the ZrB2–SiC composite with an oxide addition. An addition of Al2O3 + 32 wt.% t-ZrO2 was introduced in sufficient quantities not only to reduce the fracture stress but also to promote plastic deformation of the material for high-temperature bending strength. Study of the oxidation process showed that the weight increment of the 60 wt.% ZrB2 + 20 wt.% SiC + 20 wt.% (Al2O3 + 32 wt.% t-ZrO2) sample at 1600°C for a holding time of 1 h was stabilized by dense oxide scale formed on the material, while the weight increment of the ZrB2 + 20 wt.% SiC sample and, consequently, the scale thickness increased monotonically. The scale that formed on the ZrB2 + 20 wt.% SiC samples with an addition of Al2O3 + 32 wt.% t-ZrO2 consisted of an upper Al2SiO5-based layer 50 μm thick with ZrO2 inclusions and a lower ZrO2-based layer up to 80 μm thick with Al2SiO5 inclusions. The eutectic Al2O3 + 32 wt.% t-ZrO2 oxide addition to the basic ZrB2–SiC system had higher oxidation resistance and thus prevented the diffusion of oxygen into the material.

Corrosion Kinetics and Corrosion Mechanisms of BN–ZrO2–SiC Composites in Molten Steel

Corrosion resistance of BN–ZrO2 ceramics with different additives by molten steel

In Situ Synthesis, Mechanical Properties, and Oxidation Resistance of (sic+zrb2)/zr3[al(si)]4c6 Composites

Improving the Comprehensive Properties of ZrO2–C Materials with Aid of TiO2 Addition

Effect of the Y2O3 amount on the oxidation behavior of ZrB2-SiC-based coatings for carbon/carbon composites

Densification mechanism and corrosion resistance of h-BN/ZrO 2 ceramics prepared by spark plasma sintering

Effect of Lu2O3 addition on the oxidation behavior of SiC-ZrB2 composite coating at 1500 °C: Experimental and theoretical study

Temperature-dependent oxidation kinetics and mechanical properties degradation of Cf/ZrB2-SiC composites

Effect of Zr2Al4C5 Content on the Mechanical Properties and Oxidation Behavior of ZrB2-SiC-Zr2Al4C5 Ceramics

Mechanical and Corrosion Properties of ZrB2–SiC Composite Ceramics with Oxide Additions

Microstructure, phase evolution, mechanical properties and slag corrosion resistance of ZrO2 reinforced Al2O3–Cr2O3 composites

On corrosion of zirconium alloy in dissolved oxygen water: The role of Cu addition

Effects of H-Bn/sic Ratios on Oxidation Mechanism and Kinetics of C/C-BN-SiC Composites

Effect of boronizing treatment on the oxidation resistance of Zr2(AlSi)4C5/SiC composite

Effect of ZrO2 on sintering behavior and properties of h-BN/ZrO2 composites by spark plasma sintering

Incorporation of BN-coated carbon fibers into ZrB2/SiBCN ceramic composites and their ablation behavior

Oxidation and corrosion protection of ZG12Cr9Mo1Co1NiVNbNB (CB2) ferritic stainless steel by inorganic composite coatings at 650 °C

Revealing the influence of zirconium content on the cavitation erosion-corrosion of a wear-resistant steel in sodium chloride solution

Preparation and flame ablation/oxidation behavior of ZrB2/SiC ultra-high temperature ceramic composites

Enhanced ablative resistance of C/C composites with densified ZrB 2 -based ceramics by incorporation of Mo as interface layer

Effect of silicon on the formation of zirconium-based hybrid coatings on advanced high-strength steel surface