Microstructural stability and tensile properties of a Ti-containing single-crystal Co–Ni–Al–W-base alloy

l shi,j j yu,c y cui,x f sun

DOI: https://doi.org/10.1016/j.msea.2015.08.044

2015-01-01

Abstract:Microstructural stability and tensile properties of a Ti-containing single-crystal Co–Ni–Al–W-alloy with low tungsten content have been investigated. The alloy possesses relatively lower density and higher γ′ solvus temperature compared to some high-tungsten-content Co–Al–W-base alloys. After aging at 900–1000°C for 400 h, the alloy maintains the stable γ/γ′ two-phase microstructure without the presence of secondary phases. In the low and medium temperature range (R.T.–800°C), the alloy exhibits superior tensile strength compared to the reported single-crystal Co–Al–W-base alloys, while above 800°C, the yield stress decreases rapidly with temperature increasing. The major deformation mechanisms of the alloy consist of shearing of the γ′ precipitates by pairs of a/2〈110〉-type dislocations from room temperature to 800°C and bypassing of the γ′ precipitates by a/2〈110〉-type matrix dislocations above 900°C. At 900°C, it shows a transition from the γ′ shearing to bypassing.